Carbon Nanotube prepared by catalytic pyrolysis as the electrode for supercapacitors from polypropylene wasted face masks.

ABSTRACT

The massive global consumption and discarded face masks drove by the ongoing spread of COVID-19. Meantime, incineration and landfill discarded face masks would result in severe environmental pollution and infectious hazards. Herein a suggestion to recycle polypropylene waste masks into CNTs by an environmentally friendly and high-added value disposal process was proposed, and which was prepared as supercapacitor electrode materials for energy storage attempting. The CNTs were prepared from waste masks by catalysis pyrolysis with Ni-Fe bimetallic catalysts. Especially, the bamboo-like structure CNT was obtained with Ni/Fe molar ratio is 3. This structure owned a high specific capacitance compared to other standard CNTs. Its specific capacitance could reach 56.04 F/g (1 A/g) and has excellent cycling stability with a capacitance retention rate of the material is 85.41% after 10,000 cycles. Besides, the assembled capacitor possesses a good energy density of 4.78 Wh/kg at a power density of 900 W/kg. Thus, this work provides a sustainable and cost-effective strategy for disposing waste masks into high-valuable CNT, and their potential application for supercapacitors was also studied and exploited. It would provide a new idea for recycling and utilizing other polypropylene wastes such as medical devices.