Pure titanium samples were prepaired by CAD/CAMand casting respectively and fused with porcelain.The bond strength between tita-nium and porcelain of the samples was measured with three-point test.The titanium-porcelain interface was investigated under scanning electronic microscope(SEM).
Results:
The bond strength of CAD/CAMpure titanium to porcelain was (35.95 ±3.74)MPa and cast pure titanium to porcelain was (28.37 ±1 .98)MPa(P <0.05).SEMobservation showed that there was thin transition layer between titanium substrate and ceramic in CAD/CAM bond interface,titanium and porcelain combined closely,no obvious pores.However, there was thicker transition layer and small pore in cast pure titanium to porcelain bonding interface.