Effect of Cold-Rolling Deformation on the Microstructural and Mechanical Properties of a Biocompatible Ti-Nb-Zr-Ta-Sn-Fe Alloy.

The primary focus of the current paper centers on the microstructures and mechanical properties exhibited by a Ti-30Nb-12Zr-5Ta-2Sn-1.25Fe (wt. %) (TNZTSF) alloy that has been produced through an intricate synthesis process comprising cold-crucible induction in levitation, carried out in an atmosphere controlled by argon, and cold-rolling deformation (CR), applying systematic adjustments in the total deformation degree (total applied thickness reduction), spanning from 10% to 60%. The microstructural characteristics of the processed specimens were investigated by SEM and XRD techniques, and the mechanical properties by tensile and microhardness testing. The collected data indicate that the TNZTSF alloy's microstructure, in the as-received condition, consists of a ß-Ti phase, which shows polyhedral equiaxed grains with an average grain size close to 82.5 µm. During the cold-deformation processing, the microstructure accommodates the increased applied deformation degree by increasing crystal defects such as sub-grain boundaries, dislocation cells, dislocation lines, and other crystal defects, powerfully affecting the morphological characteristics. The as-received TNZTSF alloy showed both high strength (i.e., ultimate tensile strength close to σUTS = 705.6 MPa) and high ductility (i.e., elongation to fracture close to εf = 11.1%) properties, and the computed ß-Ti phase had the lattice parameter a = 3.304(7) Å and the average lattice microstrain ε = 0.101(3)%, which are drastically influenced by the applied cold deformation, increasing the strength properties and decreasing the ductility properties due to the increased crystal defects density. Applying a deformation degree close to 60% leads to an ultimate tensile strength close to σUTS = 1192.1 MPa, an elongation to fracture close to εf = 7.9%, and an elastic modulus close to 54.9 GPa, while the computed ß-Ti phase lattice parameter becomes a = 3.302(1) Å.

Optimizing Structural and Mechanical Properties of an Industrial Ti-6246 Alloy below ß-Transus Transition Temperature through Thermomechanical Processing.

This study aims to investigate the effect of hot deformation on commercially available Ti-6246 alloy below its ß-transus transition temperature at 900 °C, knowing that the α → ß transition temperature of Ti-6246 alloy is about 935 °C. The study systematically applies a thermomechanical processing cycle, including hot rolling at 900 °C and solution and ageing treatments at various temperatures, to investigate microstructural and mechanical alterations. The solution treatments are performed at temperatures of 800 °C, 900 °C and 1000 °C, i.e., below and above the ß-transus transition temperature, for 9 min, followed by oil quenching. The ageing treatment is performed at 600 °C for 6 h, followed by air quenching. Employing various techniques, such as X-ray diffraction, scanning electron microscopy, optical microscopy, tensile strength and microhardness testing, the research identifies crucial changes in the alloy's constituent phases and morphology during thermomechanical processing. In solution treatment conditions, it was found that at temperatures of 800 °C and 900 °C, the α'-Ti martensite phase was generated in the primary α-Ti phase according to Burger's relation, but the recrystallization process was preferred at a temperature of 900 °C, while at a temperature of 1000 °C, the α″-Ti martensite phase was generated in the primary ß-Ti phase according to Burger's relation. The ageing treatment conditions cause the α'-Ti/α″-Ti martensite phases to revert to their α-Ti/ß-Ti primary phases. The mechanical properties, in terms of strength and ductility, underwent an important beneficial evolution when applying solution treatment, followed by ageing treatment, which provided an optimal mixture of strength and ductility. This paper provides engineers with the opportunity to understand the mechanical performance of Ti-6246 alloy under applied stresses and to improve its applications by designing highly efficient components, particularly military engine components, ultimately contributing to advances in technology and materials science.

The Effect of Solution Treatment Duration on the Microstructural and Mechanical Properties of a Cold-Deformed-by-Rolling Ti-Nb-Zr-Ta-Sn-Fe Alloy.

The study presented in this paper is focused on the effect of varying the solution treatment duration on both the microstructural and mechanical properties of a cold-deformed by rolling Ti-30Nb-12Zr-5Ta-2Sn-1.25Fe (wt.%) alloy, referred to as TNZTSF. Cold-crucible induction using the levitation synthesis technique, conducted under an argon-controlled atmosphere, was employed to fabricate the TNZTSF alloy. After synthesis, the alloy underwent cold deformation by rolling, reaching a total deformation degree (total applied thickness reduction) of 60%. Subsequently, a solution treatment was conducted at 850 °C, with varying treatment durations ranging from 2 to 30 min in 2 min increments. X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques were utilized for the structural analysis, while the mechanical properties were assessed using both tensile and hardness testing. The findings indicate that (i) in both the cold-deformed-by-rolling and solution-treated states, the TNZTSF alloy exhibits a microstructure consisting of a single ß-Ti phase; (ii) in the solution-treated state, the microstructure reveals a rise in the average grain size and a decline in the internal average microstrain as the duration of the solution treatment increases; and (iii) owing to the ß-phase stability, a favorable mix of elevated strength and considerable ductility properties can be achieved.

Microstructural Considerations of a Multi-Pass Rolled Ti-Nb-Ta-Zr Alloy.

The microstructural characteristic evolution was investigated during thermomechanical processing of Ti-29Nb-9Ta-10Zr (wt %) alloy, which consisted of, in a first stage, in a Multi-Pass Rolling with increasing thickness reduction of 20%, 40%, 60%, 80%, and 90%; in step two, the multi-pass rolled sample with the highest thickness reduction (90%) was subjected to a series of three variants of static short recrystallization and then to a final similar aging. The objective was to evaluate the microstructural features evolution during thermomechanical processing (phase's nature, morphology, dimensions, and crystallographic characteristics) and to find the optimal heat treatment variant for refinement of the alloy granulation until ultrafine/nanometric level for a promising combination of mechanical properties. The microstructural features were investigated by X-ray diffraction and SEM techniques through which the presence of two phases was recorded: the ß-Ti phase and the α″-Ti martensitic phase. The corresponding cell parameters, dimensions of the coherent crystallite and the micro-deformations at the crystalline network level for both recorded phases were determined. The majority ß-Ti phase underwent a strong refinement during the Multi-Pass Rolling process until ultrafine/nano grain dimension (about 9.8 nm), with subsequent slow growing during recrystallization and aging treatments, hindered by the presence of sub-micron α″-Ti phase dispersed inside ß-Ti grains. An analysis concerning the possible deformation mechanisms was performed.

Microstructure Evolution during Hot Deformation of UNS S32750 Super-Duplex Stainless Steel Alloy.

The present paper analyzes UNS S32750 Super-Duplex Stainless Steel hot deformation behavior during processing by upsetting. The objective of this paper is to determine the optimum range of deformation temperatures, considering that both austenite and ferrite have different deformation behaviors due to their different morphology, physical, and mechanical properties. Because the capability of plastic deformation accommodation of ferrite is reduced when compared to austenite, side cracks and fissures can form during the hot deformation process. Consequently, it is important to find the optimum conditions of deformation of this type of stainless steel to establish the best processing parameters without deteriorating the material. The experimental program involved the application of hot deformation by the upsetting method on a series of samples between 1000 °C and 1275 °C, with a total degree of deformation of 30%. The resultant samples were examined by SEM-EBSD to establish and analyze the evolution of the phases present in the structure from several points of view: nature, distribution, morphology (size and shape), and their structural homogeneity. The GROD (Grain Reference Orientation Deviation) distribution map was also determined while taking into account the possible precipitation of the secondary austenite phase (γ2-phase) and the analysis of the dynamic recrystallization process according to the applied deformation temperature. The main conclusion was that UNS S32750 SDSS steel can be safely deformed by upsetting between 1050-1275 °C, with an experimented total degree of deformation of 30%.