Laser-Induced Synthesis of Tin Sulfides.

Various polytypes of van der Waals (vdW) materials can be formed by sulfur and tin, which exhibit distinctive and complementary electronic properties. Hence, these materials are attractive candidates for the design of multifunctional devices. This work demonstrates direct selective growth of tin sulfides by laser irradiation. A 532 nm continuous wave laser is used to synthesize centimeter-scale tin sulfide tracks from single source precursor tin(II) o-ethylxanthate under ambient conditions. Modulation of laser irradiation conditions enables tuning of the dominant phase of tin sulfide as well as SnS2/SnS heterostructures formation. An in-depth investigation of the morphological, structural, and compositional characteristics of the laser-synthesized tin sulfide microstructures is reported. Furthermore, laser-synthesized tin sulfides photodetectors show broad spectral response with relatively high photoresponsivity up to 4 AW-1 and fast switching time (τ rise = 1.8 ms and τ fall = 16 ms). This approach is versatile and can be exploited in various fields such as energy conversion and storage, catalysis, chemical sensors, and optoelectronics.

Laser-Synthesized 2D-MoS2 Nanostructured Photoconductors.

The direct laser synthesis of periodically nanostructured 2D transition metal dichalcogenide (2D-TMD) films, from single source precursors, is presented here. Laser synthesis of MoS2 and WS2 tracks is achieved by localized thermal dissociation of Mo and W thiosalts, caused by the strong absorption of continuous wave (c.w.) visible laser radiation by the precursor film. Moreover, within a range of irradiation conditions we have observed occurrence of 1D and 2D spontaneous periodic modulation in the thickness of the laser-synthesized TMD films, which in some cases is so extreme that it results in the formation of isolated nanoribbons with a width of ~200 nm and a length of several micrometers. The formation of these nanostructures is attributed to the effect that is known as laser-induced periodic surface structures (LIPSS), which is caused by self-organized modulation of the incident laser intensity distribution due to optical feedback from surface roughness. We have fabricated two terminal photoconductive detectors based on nanostructured and continuous films and we show that the nanostructured TMD films exhibit enhanced photo-response, with photocurrent yield increased by three orders of magnitude as compared to their continuous counterparts.

Solution-Based Synthesis of Few-Layer WS2 Large Area Continuous Films for Electronic Applications.

Unlike MoS2 ultra-thin films, where solution-based single source precursor synthesis for electronic applications has been widely studied, growing uniform and large area few-layer WS2 films using this approach has been more challenging. Here, we report a method for growth of few-layer WS2 that results in continuous and uniform films over centimetre scale. The method is based on the thermolysis of spin coated ammonium tetrathiotungstate ((NH4)2WS4) films by two-step high temperature annealing without additional sulphurization. This facile and scalable growth method solves previously encountered film uniformity issues. Atomic force microscopy (AFM) and transmission electron microscopy (TEM) were used to confirm the few-layer nature of WS2 films. Raman and X-Ray photoelectron spectroscopy (XPS) revealed that the synthesized few-layer WS2 films are highly crystalline and stoichiometric. Finally, WS2 films as-deposited on SiO2/Si substrates were used to fabricate a backgated Field Effect Transistor (FET) device for the first time using this precursor to demonstrate the electronic functionality of the material and further validate the method.