ABSTRACT
A metastable vanadium oxytelluride V2Te2O is prepared via a topochemical deintercalation of interlayer Rb+ cations in Rb1-δV2Te2O. The new ternary mixed-anion compound crystallizes in a body-centered tetragonal lattice with a = 3.9282(1) Å and c = 13.277(5) Å, containing V2O square nets that are sandwiched by Te-atomic sheets. The charge-neutral [V2OTe2] block layers stack along the c axis with van der Waals forces, which shows a metallic behavior with a dominant T2 dependence for resistivity at low temperatures. The electronic specific-heat coefficient reaches 33.9 mJ K-2 mol-1, â¼4 times that of the electronic structure calculations, suggesting a significant electron-mass renormalization. The electron correlation effect is concurrently demonstrated by the Wilson and Kadowaki-Woods ratios. Neither charge/spin-density wave nor superconductivity was observed down to 0.03 K.
ABSTRACT
We report synthesis, crystal structure and physical properties of a novel quinary compound RbGd2Fe4As4O2. The new iron oxyarsenide is isostructural to the fluo-arsenide KCa2Fe4As4F2, both of which contain separate double Fe2As2 layers that are self hole-doped in the stoichiometric composition. Bulk superconductivity at [Formula: see text] K is demonstrated by the measurements of electrical resistivity, dc magnetic susceptibility and heat capacity. An exceptionally high value of the initial slope of the upper critical field ([Formula: see text]d[Formula: see text]/d[Formula: see text] [Formula: see text] T K-1) is measured for the polycrystalline sample.
ABSTRACT
We report the synthesis, crystal structure, and physical properties of a quinary iron arsenide fluoride, KCa2Fe4As4F2. The new compound crystallizes in a body-centered tetragonal lattice (space group I4/mmm, a = 3.8684(2) Å, c = 31.007(1) Å, Z = 2) that contains double Fe2As2 conducting layers separated by insulating Ca2F2 layers. Our measurements of electrical resistivity, direct-current magnetic susceptibility, and heat capacity demonstrate bulk superconductivity at 33 K in KCa2Fe4As4F2.
ABSTRACT
A new quinary oxysulfide LaPbBiS3O was designed and successfully synthesized via a solid-state reaction in a sealed evacuated quartz tube. This material, composed of stacked NaCl-like [M4S6] (where M = Pb, Bi) layers and fluorite-type [La2O2] layers, crystallizes in the tetragonal space group P4/nmm with a = 4.0982(1) Å, c = 19.7754(6) Å, and Z = 2. Electrical resistivity and Hall effect measurements demonstrate that it is a narrow gap semiconductor with an activation energy of â¼17 meV. The thermopower and the figure of merit at room temperature were measured to be -52 µV/K and 0.23, respectively, which makes LaPbBiS3O and its derivatives be promising for thermoelectric applications.
ABSTRACT
Single crystals of a new iron-based superconductor Ba2Ti2Fe2As4O have been grown successfully via a Ba2As3-flux method in a sealed evacuated quartz tube. Bulk superconductivity with Tc â¼ 21.5 K was demonstrated in resistivity and magnetic susceptibility measurements after the as-grown crystals were annealed at 500 °C in vacuum for a week. X-ray diffraction patterns confirm that the annealed and the as-grown crystals possess the identical crystallographic structure of Ba2Ti2Fe2As4O. Energy-dispersive x-ray spectra indicate that partial Ti/Fe substitution exists in the [Fe2As2] layers and the annealing process redistributes the Ti within the Fe-plane. The ordered Fe-plane stabilized by annealing exhibits superconductivity with magnetic vortex pinned by Ti.