A comprehensive review on methods for promotion of mechanical features and biodegradation rate in amniotic membrane scaffolds.

Amniotic membrane (AM) is a biological tissue that surrounds the fetus in the mother's womb. It has pluripotent cells, immune modulators, collagen, cytokines with anti-fibrotic and anti-inflammatory effect, matrix proteins, and growth factors. In spite of the biological characteristics, some results have been released in preventing the adhesion on traumatized surfaces. Application of the AM as a scaffold is limited due to its low biomechanical resistance and rapid biodegradation. Therefore, for using the AM during surgery, its modification by different methods such as cross-linking of the membrane collagen is necessary, because the cross-linking is an effective way to reduce the rate of biodegradation of the biological materials. In addition, their cross-linking is likely an efficient way to increase the tensile properties of the material, so that they can be easily handled or sutured. In this regard, various methods related to cross-linking of the AM subsuming the composite materials, physical cross-linking, and chemical cross-linking with the glutraldehyde, carbodiimide, genipin, aluminum sulfate, etc. are reviewed along with its advantages and disadvantages in the current work.

Composite electrospun nanofibers of reduced graphene oxide grafted with poly(3-dodecylthiophene) and poly(3-thiophene ethanol) and blended with polycaprolactone.

In this paper, an effective method was employed for preparation of nanofibers using conducting polymer-functionalized reduced graphene oxide (rGO). First, graphene oxide (GO) was obtained from graphite by Hommer method. GO was reduced to rGO by NaBH4 and covalently functionalized with a 3-thiophene acetic acid (TAA) by an esterification reaction to reach 3-thiophene acetic acid-functionalized reduced graphene oxide macromonomer (rGO-f-TAAM). Afterward, rGO-f-TAAM was copolymerized with 3-dodecylthiophene (3DDT) and 3-thiophene ethanol (3TEt) to yield rGO-f-TAA-co-PDDT (rGO-g-PDDT) and rGO-f-TAA-co-P3TEt (rGO-g-PTEt), which were confirmed by Fourier transform infrared spectra. The grafted materials depicted better electrochemical properties and superior solubilities in organic solvents compared to GO and rGO. The soluble rGO-g-PDDT and rGO-g-PTEt composites blended with polycaprolactone were fabricated by electrospinning, and then cytotoxicity, hydrophilicity, biodegradability and mechanical properties were investigated. The grafted rGO composites exhibited a good electroactivity behavior, mainly because of the enhanced electrochemical performance. The electrospun nanofibers underwent degradation about 7 wt% after 40 days, and the fabricated scaffolds were not able to induce cytotoxicity in mouse osteoblast MC3T3-E1 cells. The soluble conducting composites developed in this study are utilizable in the fabrication of nanofibers with tissue engineering application.