ABSTRACT
Neodymium-doped benzil crystals have been synthesized and characterized for their absorption, emission, and kinetics properties. From Judd-Ofelt analysis, the radiative decay time of Nd emission (peaking at 1055 nm) is estimated to be equal to 441 mus. The experimental Nd lifetime (under Ar+ laser excitation) is equal to 19 mus. The broad emission band centered at approximately 700 nm (tau(decay) approximately 15 ns) and the Raman scattering with characteristic frequency shift of 1600 cm(-1) have been observed at excitation of benzil with 532-nm Q-switched laser pulses. We show that rare-earth-doped benzil can be considered as a potential candidate for luminescent and solid-state laser material.
ABSTRACT
Various optical arrangements of a double-wedge-plate shearing interferometer are presented for checking laser beam collimation. The use of moiré fringes is found to be advantageous for setting the shear fringes parallel to the direction of shear in order to obtain a well-collimated laser beam. The experimental procedure and various details of the interferometer are discussed. A brief summary of a few methods for collimation testing that use a wedge plate is also given. The accuracies achievable with shearing interferometers that use a parallel plate, a wedge plate of small angle, a double wedge having a large wedge angle, a wedge plate of large angle along with two flat mirrors, and a wedge plate having a large angle are compared and summarized.
ABSTRACT
A recipe is given for the polishing of precise surfaces oncrystals of bismuth silicate (BSO) and bismuth germanate(BGO). Using this recipe, crystals having surface figure betterthan 1/10 wave, roughness of 20-50 Å rms, and laserquality parallelism (10 arcsec or better) were obtained withabout 1-2 hours effort.