Article in English | MEDLINE | ID: mdl-31579363

ABSTRACT

Controlled growth of crosslinked polyamide (PA) thin films is demonstrated at the interface of a monomer-soaked hydrogel and an organic solution of the complementary monomer. Termed gel-liquid interfacial polymerization (GLIP), the resulting PA films are measured to be chemically and mechanically analogous to the active layer in thin film composite membranes. PA thin films are prepared using the GLIP process on both a morphologically homogeneous hydrogel prepared from poly(2-hydroxyethylmethacrylate) (PHEMA) and a phase-separated, heterogeneous hydrogel prepared from poly(acrylamide) (PAAm). Two monomer systems are examined: trimesoyl chloride (TMC) reacting with m-phenylene diamine (MPD) and TMC reacting with piperazine (PIP). Unlike the self-limiting growth behavior in TFC membrane fabrication, diffusion-limited, continuous growth of the PA films is observed, where both the thickness and roughness of the PA layers increase with reaction time. A key morphological difference is found between the two monomer systems using the GLIP process: TMC/MPD produces a ridge-and-valley surface morphology whereas TMC/PIP produces nodule/granular structures. The GLIP process represents a unique opportunity to not only explore the pore characteristics (size, spacing, and continuity) on the resulting structure and morphology of interfacially polymerized thin films, but also a method to modify the surface of (or encapsulate) hydrogels.

2.
J Memb Sci ; 5672018.
Article in English | MEDLINE | ID: mdl-30983687

ABSTRACT

It is commonly believed that the overall permeation resistance of thin film composite (TFC) membranes is dictated by the crosslinked, ultrathin polyamide barrier layer, while the porous support merely serves as the mechanical support. Although this assumption might be the case under low transmembrane pressure, it becomes questionable under high transmembrane pressure. A highly porous support normally yields under a pressure of a few MPa, which can result in a significant level of compressive strain that may significantly increase the resistance to permeation. However, quantifying the influence of porous support deformation on the overall resistance of the TFC membrane is challenging. In particular, it is difficult to determine the deformation/strain of the membrane during active separation. In this study, we use nanoimprint lithography (NIL) to achieve precise compressive deformation in commercial TFC membranes. By adjusting the NIL conditions, membranes were compressed to strain levels up to 60%. SEM and AFM measurements showed that the compression had minimal impact on the barrier-layer surface morphology and total surface area with most of the deformation occurring in the support layer. DI water permeation measurements revealed that the water flux reduction decreases with an increase of strain level. Most significantly, the intrinsic membrane resistance showed negligible changes at strain levels lower than 30%-40%, but increased exponentially at higher strain levels, reaching 250%-500% of pristine (unstrained) membrane values. Using a resistance-in-series model, the strain dependency of the TFC membrane resistance can be described.

SELECTION OF CITATIONS
SEARCH DETAIL
...