ABSTRACT
Composites made of silicon nanostructures in carbon matrixes are promising materials for anodes in Li ion batteries given the synergistic storage capacity of silicon combined with the chemical stability and electrical conductivity of carbonaceous materials. This work presents the development of Si/C composite fine fiber mats produced by carbonization of poly(vinyl alcohol) (PVA)/Si composites. PVA has a high carbon content (ca. 54.5%) and, being water-soluble, it promotes the development of environmentally friendly materials. Si nanoparticles were dispersed in PVA solutions and transformed into fine fibers using a centrifugal spinning technique given its potential for large scale production. The Si/PVA fibers mats were then subjected to dehydration by exposing them to sulfuric acid vapor. The dehydration improved the thermal and chemical stability of the PVA matrix, allowing further carbonization at 800 °C. The resulting Si/C composite fibers produced binder-free anodes for lithium ion batteries that delivered specific discharge and charge capacities of 952 mA h g-1 and 862 mA g-1, respectively, with a Columbic efficiency of 99% after 50 cycles.
ABSTRACT
Common dispersion methods such as ultrasonic sonication, planetary centrifugal mixing and magnetic dispersion have been used extensively to achieve moderate exfoliation of nanoparticles in polymer matrix. In this study, the effect of adding three roll milling to these three dispersion methods for nanoclay dispersion into epoxy matrix was investigated. A combination of each of these mixing methods with three roll milling showed varying results relative to the unmodified polymer laminate. A significant exfoliation of the nanoparticles in the polymer structure was obtained by dispersing the nanoclay combining three roll milling to magnetic and planetary centrifugal mixing methods. This exfoliation promoted a stronger interfacial bond between the matrix and the fiber, which increased the final properties of the E-glass/epoxy nanocomposite. However, a combination of ultrasound sonication and three roll milling on the other hand, resulted in poor clay exfoliation; the sonication process degraded the polymer network, which adversely affected the nanocomposite final properties relative to the unmodified E-glass/epoxy polymer.
ABSTRACT
Degradation mechanisms such as lithium plating, growth of the passivated surface film layer on the electrodes and loss of both recyclable lithium ions and electrode material adversely affect the longevity of the lithium ion battery. The anode electrode is very vulnerable to these degradation mechanisms. In this paper, the most common aging mechanisms occurring at the anode during the operation of the lithium battery, as well as some approaches for minimizing the degradation are reviewed.