ABSTRACT
The surface treatment for a polymer-ceramic composite is additionally performed in advanced material industries. To prepare the composite without a surface treatment, the simplest way to manufacture an advanced ceramic-particle is devised. The method is the formation of a nanocrystalline composite layer through the simple liquid-phase sintering. Using magnesia (MgO) which shows hydrophilicity, a nanocrystalline surface layer is realized by liquid-phase sintering. The amorphous matrix of nanocrystalline composite layer makes MgO hydrophobic and ensures miscibility with polymers, and the nanocrystalline MgO ensures high thermal conductivity. In addition, the liquid phase removes the open pores and makes the surface morphology smooth MgO with smooth surface (MgO-SM). Thermal interface materials (TIM) prepared with MgO-SM and epoxy show a high thermal conductivity of ≈7.5 W m-1 K-1 , which is significantly higher than 4.5 W m-1 K-1 of pure MgO TIM. Consequently, the formation process of a nanocrystalline surface layer utilizing simple liquid-phase sintering is proposed as a fabrication method for a next-generation ceramic-filler. In addition, it is fundamentally identified that the thermal conductivity of MgO depends on the Mg deficiency, and therefore a poly-crystal MgO-SM (produced at a low temperature) has a higher thermal conductivity than a single-crystal MgO (produced at a high temperature).
ABSTRACT
Olivine structured LiFePO4 samples were synthesized by solvothermal process using various polyol media of ethylene glycol (EG), diethylene glycol (DEG), triethylene glycol (TEG), and tetraethylene glycol (TTEG) without any heating as a post procedure. The X-ray diffraction patterns of the samples prepared in EG and DEG showed the crystalline peaks with well-fitted to the positions on the basis of an olivine type structure without any impurities. In order to determine the unit cell parameters, synchrotron powder XRD patterns were fitted with whole-pattern profile matching method using FULLPROF program. The obtained samples exhibited well dispersed nanoplate morphologies excepting for the sample prepared in EG. The samples prepared in EG, DEG, TEG, and TTEG showed the reversible capacity of 118, 167, 90, and 105 mAh/g at current density of 0.1 mA/cm2, respectively. Among them, the samples reacted in DEG and TTEG showed good performances at high rate of 16C with high capacities retention.
ABSTRACT
Hierarchically ordered mesocellular mesoporous silicas (HMMS) were swiftly synthesized using P123 and sodium silicate as a silica source within an hour by applying microwave irradiation without pore expander. The XRD, TEM and BET studies demonstrated that materials as-synthesized and calcined have the hierarchically ordered mesocellular structure with two different sizes about 10 nm and 30 nm pores having a minimized micropore volume compared with conventional hydrothermal method. Moreover, the HMMS sample prepared by microwave-assisted hydrothermal method had higher surface area than that of conventional hydrothermal method. The variation of the pore size and morphology of mesocellular structure varied with the aging time.