ABSTRACT
Bimetallic tandem catalysts have emerged as a promising strategy to locally increase the CO flux during electrochemical CO2 reduction, so as to maximize the rate of conversion to C-C-coupled products. Considering this, a novel Cu/C-Ag nanostructured catalyst has been prepared by a redox replacement process, in which the ratio of the two metals can be tuned by the replacement time. An optimum Cu/Ag composition with similarly sized particles showed the highest CO2 conversion to C2+ products compared to non-Ag-modified gas-diffusion electrodes. Gas chromatography and in-situ Raman measurements in a CO2 gas diffusion cell suggest the formation of top-bound linear adsorbed *CO followed by consumption of CO in the successive cascade steps, as evidenced by the increasingνC-H bands. These findings suggest that two mechanisms operate simultaneously towards the production of HCO2 H and C-C-coupled products on the Cu/Ag bimetallic surface.
ABSTRACT
Developing highly efficient and selective electrocatalysts for the CO2 reduction reaction to produce value-added chemicals has been intensively pursued. We report a series of Cux Oy Cz nanostructured electrocatalysts derived from a Cu-based MOF as porous self-sacrificial template. Blending catalysts with polytetrafluoroethylene (PTFE) on gas diffusion electrodes (GDEs) suppressed the competitive hydrogen evolution reaction. 25 to 50â wt % teflonized GDEs exhibited a Faradaic efficiency of ≈54 % for C2+ products at -80â mA cm-2 . The local OH- ions activity of PTFE-modified GDEs was assessed by means of closely positioning a Pt-nanoelectrode. A substantial increase in the OH- /H2 O activity ratio due to the locally generated OH- ions at increasing current densities was determined irrespective of the PTFE amount.