In Vitro Evaluation of Nanoscale Hydroxyapatite-Based Bone Reconstructive Materials with Antimicrobial Properties.

In the field of oral implantology the loss of bone tissue prevents adequate patient care, and calls for the use of synthetic biomaterials with properties that resemble natural bone. Special attention is paid to the risk of infection after the implantation of these materials. Studies have suggested that some nanocontructs containing metal ions have antimicrobial properties. The aim of this study was to examine the antimicrobial and hemolytic activity of cobalt-substituted hydroxyapatite nanoparticles, compared to hydroxyapatite and hydroxyapatite/poly-lactide-co-glycolide. The antibacterial effects of these powders were tested against two pathogenic bacterial strains: Escherichia coi (ATCC 25922) and Staphylococcus aureus (ATCC 25923), using the disc diffusion method and the quantitative antimicrobial test in a liquid medium. The quantitative antimicrobial test showed that all of the tested biomaterials have some antibacterial properties. The effects of both tests were more prominent in case of S. aureus than in E coli. A higher percentage of cobalt in the crystal structure of cobalt-substituted hydroxyapatite nanoparticles led to an increased antimicrobial activity. All of the presented biomaterial samples were found to be non-hemolytic. Having in mind that the tested of cobalt-substituted hydroxyapatite (Ca/Co-HAp) material in given concentrations shows good hemocompatibility and antimicrobial effects, along with its previously studied biological properties, the conclusion can be reached that it is a potential candidate that could substitute calcium hydroxyapatite as the material of choice for use in bone tissue engineering and clinical practices in orthopedic, oral and maxillofacial surgery.

Size effect of calcium phosphate coated with poly-DL-lactide- co-glycolide on healing processes in bone reconstruction.

In this article, synthesis and application of calcium phosphate/poly-DL-lactide-co-glycolide (CP/PLGA) composite biomaterial in particulate form, in which each CP granule/particle is coated with PLGA, are described. Two types of the particulate material having different particle sizes were synthesized: one with an average particle diameter between 150 and 250 mum (micron-sized particles, MPs) and the other with an average particle diameter smaller than 50 nm (nanoparticles, NPs). A comparative in vivo analysis was done by reconstructing defects in osteoporotic alveolar bones using both composites. The material, CP granules/particles covered with polymer, was characterized using X-ray structural analysis, scanning electron microscopy, and atomic force microscopy. Changes in reparatory functions of tissues affected by osteoporosis were examined in mice in vivo, using these two kinds of composite materials, with and without autologous plasma. Having defined the target segment, histomorphometric parameters-bone area fraction, area, and mean density-were determined. The best results in the regeneration and recuperation of alveolar bone damaged by osteoporosis were achieved with the implantation of a mixture of nanoparticulate CP/PLGA composite and autologous plasma. After the implantation of microparticulate CP/PLGA, in the form of granules, mixed with autologous plasma, into an artificial defect in alveolar bone, new bone formation was also observed, although its formation rate was slower.