Three-gradient regular solution model for simple liquids wetting complex surface topologies.

We use regular solution theory and implement a three-gradient model for a liquid/vapour system in contact with a complex surface topology to study the shape of a liquid drop in advancing and receding wetting scenarios. More specifically, we study droplets on an inverse opal: spherical cavities in a hexagonal pattern. In line with experimental data, we find that the surface may switch from hydrophilic (contact angle on a smooth surface θY < 90°) to hydrophobic (effective advancing contact angle θ > 90°). Both the Wenzel wetting state, that is cavities under the liquid are filled, as well as the Cassie-Baxter wetting state, that is air entrapment in the cavities under the liquid, were observed using our approach, without a discontinuity in the water front shape or in the water advancing contact angle θ. Therefore, air entrapment cannot be the main reason why the contact angle θ for an advancing water front varies. Rather, the contact line is pinned and curved due to the surface structures, inducing curvature perpendicular to the plane in which the contact angle θ is observed, and the contact line does not move in a continuous way, but via depinning transitions. The pinning is not limited to kinks in the surface with angles θkink smaller than the angle θY. Even for θkink > θY, contact line pinning is found. Therefore, the full 3D-structure of the inverse opal, rather than a simple parameter such as the wetting state or θkink, determines the final observed contact angle.

Controlled Fabrication of Polypyrrole Surfaces with Overhang Structures by Colloidal Templating.

Here we present the fabrication of polypyrrole (PPy) surfaces with a controlled overhang structure. Regularly structured PPy films were produced using interfacial polymerization around a sacrificial crystalline colloidal monolayer at the air/water interface. The morphology of the final inverse colloidal PPy film is controlled by the amount of monomer, the monomer: oxidant ratio and polymerization time. The PPy films exhibit an overhang structure due to depth of particle immersion in the water phase. As a result of the overhang structure, the PPy films are made hydrophobic, although the material itself is hydrophilic. The apparent contact angle of water on the structured surfaces is 109.5°, which is in agreement with the predicted contact angle using the Cassie-Baxter equation for air-filled cavities. This fabrication technique is scalable and can be readily extended to other systems where controlled wettability is required.

Enhanced adhesion of bioinspired nanopatterned elastomers via colloidal surface assembly.

We describe a scalable method to fabricate nanopatterned bioinspired dry adhesives using colloidal lithography. Close-packed monolayers of polystyrene particles were formed at the air/water interface, on which polydimethylsiloxane (PDMS) was applied. The order of the colloidal monolayer and the immersion depth of the particles were tuned by altering the pH and ionic strength of the water. Initially, PDMS completely wetted the air/water interface outside the monolayer, thereby compressing the monolayer as in a Langmuir trough; further application of PDMS subsequently covered the colloidal monolayers. PDMS curing and particle extraction resulted in elastomers patterned with nanodimples. Adhesion and friction of these nanopatterned surfaces with varying dimple depth were studied using a spherical probe as a counter-surface. Compared with smooth surfaces, adhesion of nanopatterned surfaces was enhanced, which is attributed to an energy-dissipating mechanism during pull-off. All nanopatterned surfaces showed a significant decrease in friction compared with smooth surfaces.

Facile one-step synthesis of monodisperse micron-sized latex particles with highly carboxylated surfaces.

A facile method for the aqueous synthesis of monodisperse and micronmeter-sized colloids with highly carboxylated surfaces is presented. The method is applied to three different monomers, styrene, methyl methacrylate, and 2,2,2-trifluoroethyl methacrylate, and illustrate tuning of the size and monodispersity in the reactions. High surface density of carboxylic acids of up to 10 COOH nm(-2) from potentiometric titrations, is achieved through copolymerization with itaconic acid. The versatility of this system is highlighted by creating highly fluorescent and monodisperse particles that can be index matched in aqueous solution and through surface modification via the carboxylic acid groups using standard amidation chemistry.

Physical gels based on charge-driven bridging of nanoparticles by triblock copolymers.

We have prepared an aqueous physical gel consisting of negatively charged silica nanoparticles bridged by ABA triblock copolymers, in which the A blocks are positively charged and the B block is neutral and water-soluble. Irreversible aggregation of the silica nanoparticles was prevented by precoating them with a neutral hydrophilic polymer. Both the elastic plateau modulus and the relaxation time increase slowly as the gel ages, indicating an increase both in the number of active bridges and in the strength with which the end blocks are adsorbed. The rate of this aging process can be increased significantly by applying a small shear stress to the sample. Our results indicate that charge-driven bridging of nanoparticles by triblock copolymers is a promising strategy for thickening of aqueous particle containing materials, such as water-based coatings.