ABSTRACT
Recent studies in wound dressing applications offer new therapies to promote the wound healing process. The main strategy of this study is to combine the traditional perspective of using medicinal oils with polymeric scaffolds manufactured by an engineering approach to fabricate a potential tissue engineering product that provides both new tissue formation and wound healing. Thus, Hypericum perforatum oil (HPO) and vitamin A palmitate (VAP) incorporated gelatin (Gt) nanofibrous scaffolds were successfully prepared by the electrospinning method. Tannic acid (TA) was used as the cross-linking agent. The amounts of VAP and HPO loaded in the base Gt solution [15% w/v in 4:6 v/v acetic acid/deionized water] were 5 and 50 wt % (based on the weight of Gt), respectively. The obtained scaffolds were studied regarding their microstructure, chemical structure, thermal stability, antibacterial activity, in vitro release study, and cellular proliferation assay. In the light of these studies, it was determined that VAP and HPO were incorporated successfully in Gt nanofibers cross-linked with TA. Release kinetic tests confirmed that the patterns of TA and VAP release were consistent with the Higuchi model, whereas HPO release was consistent with the first-order kinetic model. In addition, this membrane was biocompatible with L929 fibroblast cells and had antibacterial activity and thermal stability. This preliminary study suggests potential applicability of the proposed dressing to treat skin wounds in clinics.
ABSTRACT
The use of biocompatible materials and fabrication methods is of particular importance in the development of wound dressings. Cellulose acetate (CA) has excellent properties for wound dressing applications, but it is insufficient for the wound healing process due to its lack of bioactive and antibacterial properties. In this study, CA was electrospun with retinyl palmitate (RP) and clove essential oil (CLV) to fabricate a novel antibacterial and antioxidant biomaterial. The effects of RP and CLV incorporation on the surface morphology, fiber diameter, antioxidant activity, antibacterial activity, cell viability, and release behavior of the fabricated CA mats were investigated. In light of these studies, it was determined that the nanofiber mat, fabricated with a 15% w/v CA polymer concentration, a 1% w/w RP ratio, and a 5% w/w CLV ratio, was biocompatible with L929 fibroblast cells with antibacterial and antioxidant properties. Overall, results showed that this nanofiber offers promise for use as a wound dressing.
ABSTRACT
The current research was conducted to propose a nanocomposite material, which could be suitable to be used as a scaffold for bone tissue engineering applications. For this purpose, nanocomposite fibers of gelatin, poly(ε-caprolactone) (PCL), and bioactive glass were successfully fabricated via electrospinning process. In this context, response surface methodology based on a three-level, four-variable Box-Behnken design was adopted as an optimization tool to choose the most appropriate parameter settings to obtain the desired fiber diameter. The investigation, based on a second order polynomial model, focused on the analysis of the effect of both solution and processing parameters on the fiber diameter and its standard deviation. In optimum conditions (bioactive glass content of 7.5% (w/v), applied voltage of 25kV, tip-to-collector distance of 12.5cm, and flow rate of 1mL/h), the fiber diameter was found to be 584±337nm which was in good agreement with the predicted value by the developed models (523±290nm). Analytical tools such as scanning electron microscopy, X-ray diffraction analysis, Fourier transform infrared spectroscopy, and differential thermal analyzer were used for further evaluation of the optimized nanocomposite mat. The overall results showed that nanocomposite scaffolds could be promising candidates for tissue engineering applications.