ABSTRACT
Carbon nanotubes (CNTs) are synthesized by the flame fragment deposition (FFD) technique using Iraqi liquefied petroleum gas (LPG) as a source of carbon in a hand-made reactor at a low temperature (160 °C) without using a catalyst. Purification of the multi-walled carbon nanotubes (MWCNTs) is carried out using a two-step process consisting of sonication in 30 wt.% hydrogen peroxide (H2O2) solution at room temperature to remove amorphous impurities adhering to the walls of the CNTs and carbon nanoparticles (CNPs), followed by sonication in an acetone bath to remove the polyaromatic hydrocarbons (PAH) formed during the LPG gas burning. Comprehensive characterizations such as X-ray diffraction (XRD), atomic force microscopy (AFM), thermo-gravimetric analysis (TGA), and transmission electron microscopy (TEM) were conducted to verify the efficiency of the purification process. The results clearly demonstrated that this process is promising for the purification of the synthesized CNTs.
ABSTRACT
In this paper, the fabrication and growth mechanism of net-shaped micropatterned self-organized thin-film TiO2 nanotube (TFTN) arrays on a silicon substrate are reported. Electrochemical anodization is used to grow the nanotubes from thin-film titanium sputtered on a silicon substrate with an average diameter of ~30 nm and a length of ~1.5 µm using aqueous and organic-based types of electrolytes. The fabrication and growth mechanism of TFTN arrays from micropatterned three-dimensional isolated islands of sputtered titanium on a silicon substrate is demonstrated for the first time using focused-ion-beam (FIB) technique. This work demonstrates the use of the FIB technique as a simple, high-resolution, and maskless method for high-aspect-ratio etching for the creation of isolated islands and shows great promise toward the use of the proposed approach for the development of metal oxide nanostructured devices and their integration with micro- and nanosystems within silicon-based integrated-circuit devices.