ABSTRACT
Understanding the influence of co-dopants in the luminescence enhancement of carbonate glasses is the key issue in dosimetry. A series of borate glasses modified by lithium and potassium carbonate were synthesized by the melt-quenching method. The glass mixture activated with various concentrations of TiO2 and MgO was subjected to various doses of gamma-rays ((60)Co). The amorphous nature of the samples was confirmed by x-ray diffraction (XRD) spectra. The simple glowing curve of the glass doped with TiO2 features a peak at 230°C, whose intensity is maximal at 0.5 mol% of the dopant. The intensity of the glowing curve increases with the concentration of MgO added as a co-dopant up to 0.25 mol%, where it is two times higher than for the material without MgO thermoluminescence properties, including dose response, reproducibility, and fading were studied. The effective atomic number of the material was also determined. Kinetic parameters, such as kinetics order, activation energy, and frequency factor are estimated. The photoluminescence spectra of the titanium-doped glass consist of a prominent peaks at 480 nm when laser excitation at 650 nm is used. A three-fold photoluminescence enhancement and a blue shift of the peak were observed when 0.1% MgO was introduced. In addition, various physical parameters, such as ion concentration, polaron radius and internuclear distances were calculated. The mechanism for the thermoluminescence and photoluminescence enhancements are discussed.
ABSTRACT
The thermoluminescent properties of boric glass modified with lithium and potassium carbonates (LKB) and co-doped with CuO and MgO are reported for the first time. Two techniques are applied to investigate the effect of dopants and co-dopants on the thermal stimulation properties of LKB. The induced TL glow curves of a CuO-doped sample are found to be at 220°C with a single peak. An enhancement of about three times is shown with the increment of 0.1 mol % MgO as a co-dopant impurity. This enhancement may contribute to the ability of magnesium to create extra electron traps and consequently the energy transfer to monovalent Cu(+) ions. LKB:Cu,Mg is low Z material (Zeff=8.55), and observed 15 times less sensitive than LiF: Mg, Ti (TLD-100). The proposed dosemeter showed good linearity in TL dose-response, low fading and excellent reproducibility with a simple glow curve, and thus, can be used in the radiation dosimetry.