ABSTRACT
The influence of rare earth (RE) elements on superconducting properties of the transition element (TE)-substituted TE xCu1- xSr2RECu2O y cuprates has not been sufficiently emphasized so far. In the case of molibdo-cuprates with the general formula Mo0.3Cu0.3Sr2RECu2O y, all the RE element containing compounds except La, Ce, and Lu can be prepared at room pressure. The influence of the crystal structure on the superconducting properties after ozone oxidation of the present system is reported selecting three groups of RE elements attending to their different atom sizes: small (Yb and Tm), medium (Gd), and big (Nd and Pr). Advanced transmission electron microscopy, various diffraction techniques, and spectroscopic analysis have been used to demonstrate that the increase of structural disorder complemented with a decrease in the hole content play a major role in the vanishing of superconductivity within the present system.
ABSTRACT
A novel ScVO(3) perovskite phase has been synthesized at 8 GPa and 1073 K from the cation-disordered bixbyite-type ScVO(3). The new perovskite has orthorhombic symmetry at room temperature, space group Pnma, and lattice parameters a = 5.4006(2) Å, b = 7.5011(2) Å, and c = 5.0706(1) Å with Sc(3+) and V(3+) ions fully ordered on the A and B sites of the perovskite cell. The vanadium oxygen octahedra [V-O(6)] display cooperative Jahn-Teller (JT) type distortions, with predominance of the tetragonal Q(3) over the orthorhombic Q(2) JT modes. The orthorhombic perovskite shows Arrhenius-type electrical conductivity and undergoes a transition to triclinic symmetry space group P-1 close to 90 K. Below 60 K, the magnetic moments of the 4 nonequivalent vanadium ions undergo magnetic long-range ordering, resulting in a magnetic superstructure of the perovskite cell with propagation vector (0.5, 0, 0.5). The magnetic moments are confined to the xz plane and establish a close to zigzag antiferromagnetic mode.
ABSTRACT
The corundum-type In(2-2x)Zn(x)Sn(x)O(3) solid solution (cor-ZITO, x ≤ 0.7) was synthesized at 1000 °C under a high pressure of 70 kbar. cor-ZITO is a high-pressure polymorph of the transparent conducting oxide bixbyite-In(2-2x)Zn(x)Sn(x)O(3) (x ≤ 0.4). Analysis of the extended X-ray absorption fine structure suggests that significant face-sharing of Zn and Sn octahedra occurs, as expected for the corundum structure type. In contrast to the ideal corundum structure, however, Zn and Sn are displaced and form oxygen bonds with lengths that are similar to those observed in high-pressure ZnSnO(3). Powder X-ray diffraction patterns of cor-ZITO showed the expected unit cell contraction with increased cosubstitution, but no evidence for ilmenite-type ordering of the substituted Zn and Sn. A qualitative second harmonic generation measurement, for the solid solution x = 0.6 and using 1064 nm radiation, showed that Zn and Sn adopt a polar LiNbO(3)-type arrangement.