ABSTRACT
Objective: The aim of this study was to carry out an in vivo assessment of bone ingrowth in two different typesof porous titanium -the first being completely porous, and the second with a porous surface and dense nucleus,manufactured by powder metallurgy- and to evaluate their mechanical properties. Study design: Ten scaffoldsfrom each group were submitted to metallographic analysis and compression tests. Next, two scaffolds of eachtype were inserted into 14 rabbits, which were sacrificed 8 weeks after surgery. The samples were submitted forhistological examination. Results: Metallographic analysis revealed interconnected pores, and the average interconnectedpore diameter was about 360 mm, with 36% total porosity. The totally porous titanium samples and thetitanium samples with porous surface and dense nucleus showed an average compressive strength of 16.19 MPaand 69.27 MPa, respectively. After 8 weeks, the animals showed bone ingrowth, even into the most internal pores.Conclusions: The pore morphology was effective in permitting bone ingrowth in both groups. Titanium scaffoldswith a porous surface and dense nucleus showed the best mechanical properties and most adequate interface (AU)