Room-temperature atomic layer deposition of SiO2 on microcracked ZrO2 layers.

Yttria-stabilized zirconia (Y-SZ) has become a reliable material option to restore severely compromised teeth. Y-SZ materials are prone to low-temperature degradation (LTD), which generates a tetragonal-to-monoclinic (t-m) transformed, porous layer. We suggest that room-temperature atomic layer deposition (RT-ALD) could be used for the infiltration and deposition of nanoscale SiO2 film over this layer, creating a protective hybrid surface against further degradation by LTD. This study investigated the potential of developing a Y-SZ transformed layer under controlled conditions for the infiltration of silica using RT-ALD, aiming to develop a hybrid zirconia-silica interface, and to investigate the effect of silica deposition/infiltration via RT-ALD on the surface roughness and wettability of zirconia-based materials. Sintered specimens (14 mm × 4 mm x 2 mm) were prepared from four different Y-SZ materials (n = 40): low translucency 3 mol % Y-SZ (3Y-LT; Ceramill ZI, Amann Girrbach); high translucency 4 mol % Y-SZ (4Y-HT; Ceramill Zolid); and two high translucency 5 mol % Y-SZ (5Y-HT - Lava Esthetic, 3M; 5Y-SHT - Ceramill Zolid, FX white). Specimens were exposed to hydrothermal treatment (HTT) to develop similar depths of crystalline changes. RT-ALD was used to deposit a thin film of silica (SiO2). Surface roughness and wettability analyses were performed to investigate the effect of treatment (HTT and RT-ALD) and material on Y-SZ surface properties, and data was analyzed by two-way ANOVA and Tukey HSD (p < 0.05). RT-ALD and HTT-RT-ALD treated specimens of 3Y-LT and 5Y-HT materials were exposed to further hydrothermal aging (HA) and the surface was characterized by time-of-flight secondary ion mass spectrometry (ToF-SIMS). There was a significant interaction effect of material and treatment (HTT and RT-ALD) on roughness (p = 0.02), and surface wettability (p < 0.001). Silica deposition via RT-ALD resulted in a significant increase in surface roughness of all materials tested, while surface wettability was either improved or not changed based on the material type and HTT exposure. Nanofilms of SiO2 were successfully deposited on Y-SZ materials and infiltrated 3Y-LT zirconia.

Surface and bulk properties of zirconia as a function of composition and aging.

Yttria-stabilized zirconia (Y-SZ) materials with different levels of translucency have been used for indirect dental restorations. Y-SZ composition and microstructure are modified to improve translucency, and it is not clear how these materials respond to aging. This study evaluated the effect of hydrothermal aging (HA) performed in an autoclave on the properties of four dental Y-SZ materials with different compositions. Sintered bar-shaped specimens (14 x 4 x 2 mm) were prepared from four different zirconia-based materials (n = 40): low translucency 3 mol % Y-SZ (3Y-LT; Ceramill ZI, Amann Girrbach); high translucency 4 mol % Y-SZ (4Y-HT; Ceramill Zolid); and two high translucency 5 mol % Y-SZ (5Y-HT - Lava Esthetic, 3M; 5Y-SHT - Ceramill Zolid FX). Fully sintered specimens were exposed to HA for different times (control - 0 h, 5 h, 10 h, or 15 h at 134 °C, 2 bar pressure) and characterized for surface roughness, flexural strength (three-point bending), hardness and elastic modulus (nanoindentation), surface wettability (sessile drop technique) and crystalline content (x-ray diffraction, XRD). Data was analyzed by two-way ANOVA and Tukey HSD (p < 0.05). Zirconia composition significantly affected roughness (p = 0.016). Zirconia*aging interaction affected flexural strength (p = 0.012), surface wettability (p < 0.001), and hardness (p = 0.002). Zirconia composition (p = 0.011) and aging (p = 0.001) affected elastic modulus, while the interaction effect was not significant (p = 0.94). HA affects zirconia-based materials in different degrees. For 3Y-LT and 4Y-HT, surface and bulk properties were affected by aging to a similar extent. However, surface and bulk properties may change during clinical use as a result of prolonged degradation of Y-SZ.