Green metal oxides coated biochar nanocomposites preparation and its utilization in vertical flow constructed wetlands for reactive dye removal: Performance and kinetics studies.

Major causes of water pollution in the ecosystem are pollutants such as dyes which are noxious. The present study was based on the synthesis of the green nano-biochar composites from cornstalk and green metal oxide resulting in Copper oxide/biochar, Zinc oxide /biochar, Magnesium oxide/biochar, Manganese oxide/biochar, biochar for removal of dyes combined with the constructed wetland (CW). Biochar Augmentation in constructed wetland systems has improved dye removal efficiency to 95% in order of copper oxide/biochar > Magnesium oxide/biochar > Zinc oxide/biochar > Manganese oxide/biochar > biochar > control (without biochar) respectively in wetlands. It has increased the efficiency of pH by maintaining pH 6.9-7.4, while Total Suspended Solids (TSS) removal efficiency and Dissolved oxygen (DO) increased with the hydraulic retention time of about 7 days for 10 weeks. Chemical oxygen demand (COD) and colour removal efficiency increased with the hydraulic retention time of 12 days for 2 months and there was a low removal efficiency for total dissolved solids (TDS) from control (10.11%) to Copper oxide /biochar (64.44%) and Electrical conductivity (EC) from control (8%) to Copper oxide /biochar (68%) with the hydraulic retention time of about 7 days for 10 weeks. Colour and chemical oxygen demand removal kinetics followed second and first-order kinetic. A significant growth in the plants were also observed. These results proposed the use of agricultural waste-based biochar as part of a constructed wetland substratum can provide enhanced removal of textile dyes. That can be reused.

Structural and optical properties of ITO/TiO2 anti-reflective films for solar cell applications.

Indium tin oxide (ITO) and titanium dioxide (TiO2) anti-reflective coatings (ARCs) were deposited on a (100) P-type monocrystalline Si substrate by a radio-frequency (RF) magnetron sputtering. Polycrystalline ITO and anatase TiO2 films were obtained at room temperature (RT). The thickness of ITO (60 to 64 nm) and TiO2 (55 to 60 nm) films was optimized, considering the optical response in the 400- to 1,000-nm wavelength range. The deposited films were characterized by X-ray diffraction (XRD), Raman spectroscopy, field emission scanning electron microscopy (FESEM), energy dispersive spectroscopy (EDS), and atomic force microscopy (AFM). The XRD analysis showed preferential orientation along (211) and (222) for ITO and (200) and (211) for TiO2 films. The XRD analysis showed that crystalline ITO/TiO2 films could be formed at RT. The crystallite strain measurements showed compressive strain for ITO and TiO2 films. The measured average optical reflectance was about 12% and 10% for the ITO and TiO2 ARCs, respectively.