Advanced Hollow Cathode Discharge Plasma Treatment of Unique Bilayered Fibrous Nerve Guidance Conduits for Enhanced/Oriented Neurite Outgrowth.

Despite all recent progresses in nerve tissue engineering, critical-sized nerve defects are still extremely challenging to repair. Therefore, this study targets the bridging of critical nerve defects and promoting an oriented neuronal outgrowth by engineering innovative nerve guidance conduits (NGCs) synergistically possessing exclusive topographical, chemical, and mechanical cues. To do so, a mechanically adequate mixture of polycaprolactone (PCL) and polylactic-co-glycolic acid (PLGA) was first carefully selected as base material to electrospin nanofibrous NGCs simulating the extracellular matrix. The electrospinning process was performed using a newly designed 2-pole air gap collector that leads to a one-step deposition of seamless NGCs having a bilayered architecture with an inner wall composed of highly aligned fibers and an outer wall consisting of randomly oriented fibers. This architecture is envisaged to afford guidance cues for the extension of long neurites on the underlying inner fiber alignment and to concurrently provide a sufficient nutrient supply through the pores of the outer random fibers. The surface chemistry of the NGCs was then modified making use of a hollow cathode discharge (HCD) plasma reactor purposely designed to allow an effective penetration of the reactive species into the NGCs to eventually treat their inner wall. X-ray photoelectron spectroscopy (XPS) results have indeed revealed a successful O2 plasma modification of the inner wall that exhibited a significantly increased oxygen content (24 → 28%), which led to an enhanced surface wettability. The treatment increased the surface nanoroughness of the fibers forming the NGCs as a result of an etching effect. This effect reduced the ultimate tensile strength of the NGCs while preserving their high flexibility. Finally, pheochromocytoma (PC12) cells were cultured on the NGCs to monitor their ability to extend neurites which is the base of a good nerve regeneration. In addition to remarkably improved cell adhesion and proliferation on the plasma-treated NGCs, an outstanding neural differentiation occurred. In fact, PC12 cells seeded on the treated samples extended numerous long neurites eventually establishing a neural network-like morphology with an overall neurite direction following the alignment of the underlying fibers. Overall, PCL/PLGA NGCs electrospun using the 2-pole air gap collector and O2 plasma-treated using an HCD reactor are promising candidates toward a full repair of critical nerve damage.

Multifaceted polymeric nerve guidance conduits with distinctive double-layered architecture and plasma-induced inner chemistry gradient for the repair of critical-sized defects.

Despite tissue engineering advances, current nerve guidance conduits (NGCs) are still failing in repairing critical-sized defects. This study aims, therefore, at tackling large nerve gaps (2 cm) by designing NGCs possessing refined physicochemical properties enhancing the activity of Schwann cells (SCs) that support nerve regeneration over long distances. As such, a combinatorial strategy adopting novel plasma-induced surface chemistry and architectural heterogeneity was considered. A mechanically suitable copolymer (Polyactive®) was electrospun to produce nanofibrous NGCs mimicking the extracellular matrix. An innovative seamless double-layered architecture consisting of an inner wall comprised of bundles of aligned fibers with intercalated random fibers and an outer wall fully composed of random fibers was conceived to synergistically provide cell guidance cues and sufficient nutrient inflow. NGCs were subjected to argon plasma treatments using a dielectric barrier discharge (DBD) and a plasma jet (PJ). Surface chemical changes were examined by advanced X-ray photoelectron spectroscopy (XPS) micro-mappings. The DBD homogeneously increased the surface oxygen content from 17 % to 28 % on the inner wall. The PJ created a gradient chemistry throughout the inner wall with an oxygen content gradually increasing from 21 % to 30 %. In vitro studies revealed enhanced primary SC adhesion, elongation and proliferation on plasma-treated NGCs. A cell gradient was observed on the PJ-treated NGCs thus underlining the favorable oxygen gradient in promoting cell chemotaxis. A gradual change from circular to highly elongated SC morphologies mimicking the bands of Büngner was visualized along the gradient. Overall, plasma-treated NGCs are promising candidates paving the way towards critical nerve gap repair.

Polylactic Acid/Polyaniline Nanofibers Subjected to Pre- and Post-Electrospinning Plasma Treatments for Refined Scaffold-Based Nerve Tissue Engineering Applications.

Composite biopolymer/conducting polymer scaffolds, such as polylactic acid (PLA)/ polyaniline (PAni) nanofibers, have emerged as popular alternative scaffolds in the electrical-sensitive nerve tissue engineering (TE). Although mimicking the extracellular matrix geometry, such scaffolds are highly hydrophobic and usually present an inhomogeneous morphology with massive beads that impede nerve cell-material interactions. Therefore, the present study launches an exclusive combinatorial strategy merging successive pre- and post-electrospinning plasma treatments to cope with these issues. Firstly, an atmospheric pressure plasma jet (APPJ) treatment was applied on PLA and PLA/PAni solutions prior to electrospinning, enhancing their viscosity and conductivity. These liquid property changes largely eliminated the beaded structures on the nanofibers, leading to uniform and nicely elongated fibers having average diameters between 170 and 230 nm. After electrospinning, the conceived scaffolds were subjected to a N2 dielectric barrier discharge (DBD) treatment, which significantly increased their surface wettability as illustrated by large decreases in water contact angles for values above 125° to values below 25°. X-ray photoelectron spectroscopy (XPS) analyses revealed that 3.3% of nitrogen was implanted on the nanofibers surface in the form of C-N and N-C=O functionalities upon DBD treatment. Finally, after seeding pheochromocytoma (PC-12) cells on the scaffolds, a greatly enhanced cell adhesion and a more dispersive cell distribution were detected on the DBD-treated samples. Interestingly, when the APPJ treatment was additionally performed, the extension of a high number of long neurites was spotted leading to the formation of a neuronal network between PC-12 cell clusters. In addition, the presence of conducting PAni in the scaffolds further promoted the behavior of PC-12 cells as illustrated by more than a 40% increase in the neurite density without any external electrical stimulation. As such, this work presents a new strategy combining different plasma-assisted biofabrication techniques of conducting nanofibers to create promising scaffolds for electrical-sensitive TE applications.

Biological activity and antimicrobial property of Cu/a-C:H nanocomposites and nanolayered coatings on titanium substrates.

Infection associated with titanium based implants remains the most serious problem in implant surgery hence it is important to find optimal strategies to prevent infections. In the present study, we investigated the surface properties, antibacterial activity and biocompatibility of nanocomposite coatings based on an amorphous hydrocarbon (a-C:H) film containing copper nanoparticles (CuNPs) deposited on Ti discs via a gas aggregation cluster source. Three different Cu/a-C:H coatings with approximately the same amount of embedded CuNPs with and without barrier a-C:H layer were fabricated. The obtained results revealed that different structures of the produced coatings have significantly different release rates of Cu ions from the coatings into the aqueous media. This subsequently influences the antibacterial efficiency and osteoblast cell viability of the treated coatings. Coatings with the highest number of CuNPs resulted in excellent antibacterial activity exhibiting approximately 4 log reduction of E.coli and S.aureus after 24 h incubation. The cytotoxicity study revealed that after 7 day cell seeding, even the coating with the highest Cu at.% (4 at.%) showed a cell viability of Ì´90%. Consequently, the coating, formed with a properly tailored number of CuNPs and a-C:H barrier thickness offer a strong antibacterial effect without any harm to osteoblast cells.

Investigation of Ag/a-C:H Nanocomposite Coatings on Titanium for Orthopedic Applications.

One of the leading causes of failure for any bone implant is implant-associated infections. The implant-bone interface is in fact the crucial site of infection where both the microorganisms and cells compete to populate the newly introduced implant surface. Most of the work dealing with this issue has focused on the design of implant coatings capable of preventing infection while ignoring cell proliferation or vice versa. The present study is therefore focused on investigating the antibacterial and biological properties of nanocomposite coatings based on an amorphous hydrocarbon (a-C:H) matrix containing silver nanoparticles (AgNPs). a-C:H coatings with varying silver concentrations were generated directly on medical grade titanium substrates using a combination of a gas aggregation source (GAS) and a plasma-enhanced chemical vapor deposition (PE-CVD) process. The obtained results revealed that the surface silver content increased from 1.3 at % to 5.3 at % by increasing the used DC magnetron current in the GAS from 200 to 500 mA. The in vitro antibacterial assays revealed that the nanocomposites with the highest number of silver content exhibited excellent antibacterial activities resulting in a 6-log reduction of Escherichia coli and a 4-log reduction of Staphylococcus aureus after 24 h of incubation. An MTT assay, fluorescence live/dead staining, and SEM microscopy observations of MC3T3 cells seeded on the uncoated and coated Ti substrates also showed that increasing the amount of AgNPs in the nanocomposites had no notable impact on their cytocompatibility, while improved cell proliferation was especially observed for the nanocomposites possessing a low amount of AgNPs. These controllable Ag/a-C:H nanocomposites on Ti substrates, which simultaneously provide an excellent antibacterial performance and good biocompatibility, could thus have promising applications in orthopedics and other biomedical implants.