ABSTRACT
Cerium oxide nanoparticles (CeO2-NPs) have great applications in different industries, including nanomedicine. However, some studies report CeO2-NPs-related toxicity issues that limit their usage and efficiency. In this study, the sol-gel method was applied to the synthesis of CeO2-NPs using poly(allylamine) (PAA) as a capping and/or stabilizing agent. The different molecular weights of PAA (15,000, 17,000, and 65,000 g/mol) were used to investigate the physico-chemical and biological properties of the NPs. In order to understand their performance as an anticancer agent, three cell lines (MCF7, HeLa, and erythrocyte) were analyzed by MTT assay and RBC hemolysis assay. The results showed that the CeO2-NPs had anticancer effects on the viability of MCF7 cells with half-maximal inhibitory concentration (IC50) values of 17.44 ± 7.32, 6.17 ± 1.68, and 0.12 ± 0.03 µg/mL for PAA15000, PAA17000, PAA65000, respectively. As for HeLa cells, IC50 values reduced considerably to 8.09 ± 1.55, 2.11 ± 0.33, and 0.20 ± 0.01 µg/mL, in order. A decrease in the viability of cancer cells was associated with the 50% hemolytic concentration (HC50) of 0.022 ± 0.001 mg/mL for PAA15000, 3.74 ± 0.58 mg/mL for PAA17000, and 7.35 ± 1.32 mg/mL for PAA65000. Ultraviolet-Visible (UV-vis) spectroscopy indicated that an increase in the PAA molecular weight led to a blue shift in the bandgap and high amounts of Ce3+ on the surface of the nanoceria. Thus, PAA65000 could be considered as a biocompatible nanoengineered biomaterial for potential applications in cancer nanomedicine.
ABSTRACT
OBJECTIVES: Esophageal squamous cell carcinoma (ESCC) is considered as a deadly medical condition that affects a growing number of people worldwide. Targeted therapy of ESCC has been suggested recently and required extensive research. With cyclin D1 as a therapeutic target, the present study aimed at evaluating the anticancer effects of doxorubicin (Dox) or Hypericum perforatum L. (HP) extract encapsulated in poly(lactic-co-glycolic acid) (PLGA) nanoparticles on the ESCC cell line KYSE30. METHODS: Nanoparticles were prepared using double emulsion method. Cytotoxicity assay was carried out to measure the anti-proliferation activity of Dox-loaded (Dox NPs) and HP-loaded nanoparticles (HP NPs) against both cancer and normal cell lines. The mRNA gene expression of cyclin D1 was evaluated to validate the cytotoxicity studies at molecular level. RESULTS: Free drugs and nanoparticles significantly inhibited KYSE30 cells by 55-73% and slightly affected normal cells up to 29%. The IC50 of Dox NPs and HP NPs was ~ 0.04-0.06 mg/mL and ~ 0.6-0.7 mg/mL, respectively. Significant decrease occurred in cyclin D1 expression by Dox NPs and HP NPs (P < 0.05). Exposure of KYSE-30 cells to combined treatments including both Dox and HP extract significantly increased the level of cyclin D1 expression as compared to those with individual treatments (P < 0.05). CONCLUSION: Dox NPs and HP NPs can successfully and specifically target ESCC cells through downregulation of cyclin D1. The simultaneous use of Dox and HP extract should be avoided for the treatment of ESCC.
ABSTRACT
BACKGROUND: In recent years, prostate cancer prevails as one of the lead cancers affecting men. Currently, prostate cancer research involves the phytochemical study of plants with anti-tumour effects. This study compares the anti-tumour effects of three plant species indigenous to Iran and their interaction with cluster of differentiation (CD)-82 protein, a therapeutic target found in prostate cancer cells. METHODS: The extracts of Hypericum perforatum, Achillea millefolium, and Aloe vera were prepared and their toxicological, cellular and gene expression responses were evaluated in PC-3 human prostate cancer cells and normal human chondrocyte cell line C28/I2. They were exposed to different concentrations of the plants (10 mg/mL, 5 mg/mL, 1 mg/mL, 100 µg/mL, 10 µg/mL, and 1 µg/mL) at three exposure time points (24, 48, 72 hours) to determine cancer cell cytotoxicity and gene expression profiles. RESULTS: : Half-maximal inhibitory concentration (IC50) in PC-3 cells ranged from 0.6 to 8.5 mg/mL for H. perforatum extract, from 0.4 to 7.5 mg/mL for A. Millefolium extract, and from 0.2 to 8.0 mg/mL for A. vera extract in a time-dependent manner. A. vera extract caused the highest cell death levels in PC-3 cells (94%) and C28/I2 cells (57%) after 48 hours. A 1.97-, 3.00-, and 3.48-fold increase in relative gene expression of CD82 was observed for H. perforatum, A. millefolium, and A. vera extracts, respectively. CONCLUSION: A. vera and A. millefolium extracts are a selective inhibitor of prostate cancer cells and a potent activator of CD82 expression.
ABSTRACT
Attempts have been made to prepare nanoparticles based on poly(lactic-co-glycolic acid) (PLGA) and doxorubicin. Biological evaluation and physio-chemical characterizations were performed to elucidate the effects of initial drug loading and polymer composition on nanoparticle properties and its antitumor activity. PLGA nanoparticles were formulated by sonication method. Lactide/glycolide ratio and doxorubicin amounts have been tailored. Fourier transform infrared spectroscopy (FTIR) and differential scanning calorimetry (DSC) were employed to identify the presence of doxorubicin within nanospheres. The in vitro release studies were performed to determine the initial ant net release rates over 24 h and 20 days, respectively. Furthermore, cytotoxicity assay was measured to evaluate therapeutic potency of doxorubicin-loaded nanoparticles. Spectroscopy and thermal results showed that doxorubicin was loaded into the particles successfully. It was observed that lactide/glycolide content of PLGA nanoparticles containing doxorubicin has more prominent role in tuning particle characteristics. Doxorubicin release profiles from PLGA 75 nanospheres demonstrated that the cumulative release rate increased slightly and higher initial burst was detected in comparison to PLGA 50 nanoparticles. MTT data revealed doxorubicin induced antitumor activity was enhanced by encapsulation process, and increasing drug loading and glycolide portion. The results led to the conclusion that by controlling the drug loading and the polymer hydrophilicity, we can adjust the drug targeting and blood clearance, which may play a more prominent role for application in chemotherapy.
ABSTRACT
BACKGROUND: Substrates in medical science are hydrophilic polymers undergoing volume expansion when exposed to culture medium that influenced on cell attachment. Although crosslinking by chemical agents could reduce water uptake and promote mechanical properties, these networks would release crosslinking agents. In order to overcome this weakness, silicone rubber is used and reinforced by nanoclay. OBJECTIVES: Attempts have been made to prepare nanocomposites based on medical grade HTV silicone rubber (SR) and organo-modified montmorillonite (OMMT) nanoclay with varying amounts of clay compositions. MATERIALS AND METHODS: Incorporation of nanocilica platelets into SR matrix was carried out via melt mixing process taking advantage of a Brabender internal mixer. The tensile elastic modulus of nanocomposites was measured by performing tensile tests on the samples. Produced polydimetylsiloxane (PDMS) composites with different flexibilities and crosslink densities were employed as substrates to investigate biocompatibility, cell compaction, and differential behaviors. RESULTS: The results presented here revealed successful nanocomposite formation with SR and OMMT, resulting in strong PDMS-based materials. The results showed that viability, proliferation, and spreading of cells are governed by elastic modulus and stiffness of samples. Furthermore, adipose derived stem cells (ADSCs) cultured on PDMS and corresponding nanocomposites could retain differentiation potential of osteocytes in response to soluble factors, indicating that inclusion of OMMT would not prevent osteogenic differentiation. Moreover, better spread out and proliferation of cells was observed in nanocomposite samples. CONCLUSIONS: Considering cell behavior and mechanical properties of nanobiocomposites it could be concluded that silicone rubber substrate filled by nanoclay are a good choice for further experiments in tissue engineering and medical regeneration due to its cell compatibility and differentiation capacity.