ABSTRACT
The effects of holding time and Si on the content, shape size and structure of Ti2Al20La phase in Al-Ti-La intermediate alloy were investigated by an X-ray diffractometer, scanning electron microscope and transmission electron microscope. The results show that the volume fraction and aspect ratio of Ti2Al20La phase in Al-Ti-La intermediate alloy decrease significantly, from 21% and 2.3 without Si addition to 4% and 2.0 with the addition of 2.3 wt.% Si at a holding time of 15 min at 750 °C, respectively. The Si element will attach to the Ti2Al20La phase and form La-Si binary phase at the grain boundary of α-Al. With the increase of holding time from 15 min to 60 min, the content of Ti2Al20La phase in the alloy gradually decreases and the size decreases significantly. Meanwhile, Al11La3 will dissolve and disappear, while the content of La-Si binary phase increases, and part of Ti2Al20La phase transforms into Ti2(Al20-x,Six)La phase.