ABSTRACT
A surface plasmon (SP)-enhanced nanoporous GaN-based green LED based on top-down processing technology has been successfully fabricated. This SP-enhanced LED consists of nanopores passing through the multiple quantum wells (MQWs) region, with Ag nanorod array filled in the nanopores for SP-MQWs coupling and thin Al(2)O(3) passivation layer for electrical protection. Compared with nanoporous LED without Ag nanorods, the electroluminescence (EL) peak intensity for the SP-enhanced LED was greatly enhanced by 380% and 220% at an injection current density of 1 and 20A/cm(2), respectively. Our results show that the increased EL intensity is mainly attributed to the improved internal quantum efficiency of LED due to the SP coupling between Ag nanorods and MQWs.