Optimizing Structural and Mechanical Properties of an Industrial Ti-6246 Alloy below ß-Transus Transition Temperature through Thermomechanical Processing.

This study aims to investigate the effect of hot deformation on commercially available Ti-6246 alloy below its ß-transus transition temperature at 900 °C, knowing that the α → ß transition temperature of Ti-6246 alloy is about 935 °C. The study systematically applies a thermomechanical processing cycle, including hot rolling at 900 °C and solution and ageing treatments at various temperatures, to investigate microstructural and mechanical alterations. The solution treatments are performed at temperatures of 800 °C, 900 °C and 1000 °C, i.e., below and above the ß-transus transition temperature, for 9 min, followed by oil quenching. The ageing treatment is performed at 600 °C for 6 h, followed by air quenching. Employing various techniques, such as X-ray diffraction, scanning electron microscopy, optical microscopy, tensile strength and microhardness testing, the research identifies crucial changes in the alloy's constituent phases and morphology during thermomechanical processing. In solution treatment conditions, it was found that at temperatures of 800 °C and 900 °C, the α'-Ti martensite phase was generated in the primary α-Ti phase according to Burger's relation, but the recrystallization process was preferred at a temperature of 900 °C, while at a temperature of 1000 °C, the α″-Ti martensite phase was generated in the primary ß-Ti phase according to Burger's relation. The ageing treatment conditions cause the α'-Ti/α″-Ti martensite phases to revert to their α-Ti/ß-Ti primary phases. The mechanical properties, in terms of strength and ductility, underwent an important beneficial evolution when applying solution treatment, followed by ageing treatment, which provided an optimal mixture of strength and ductility. This paper provides engineers with the opportunity to understand the mechanical performance of Ti-6246 alloy under applied stresses and to improve its applications by designing highly efficient components, particularly military engine components, ultimately contributing to advances in technology and materials science.

Evolution of Microstructural and Mechanical Properties during Cold-Rolling Deformation of a Biocompatible Ti-Nb-Zr-Ta Alloy.

In this study, a Ti-32.9Nb-4.2Zr-7.5Ta (wt%) titanium alloy was produced by melting in a cold crucible induction in a levitation furnace, and then deforming by cold rolling, with progressive deformation degrees (thickness reduction), from 15% to 60%, in 15% increments. The microstructural characteristics of the specimens in as-received and cold-rolled conditions were determined by XRD and SEM microscopy, while the mechanical characteristics were obtained by tensile and microhardness testing. It was concluded that, in all cases, the Ti-32.9Nb-4.2Zr-7.5Ta (wt%) showed a bimodal microstructure consisting of Ti-ß and Ti-α″ phases. Cold deformation induced significant changes in the microstructural and the mechanical properties, leading to grain-refinement, crystalline cell distortions and variations in the weight-fraction ratio of both Ti-ß and Ti-α″ phases, as the applied degree of deformation increased from 15% to 60%. Changes in the mechanical properties were also observed: the strength properties (ultimate tensile strength, yield strength and microhardness) increased, while the ductility properties (fracture strain and elastic modulus) decreased, as a result of variations in the weight-fraction ratio, the crystallite size and the strain hardening induced by the progressive cold deformation in the Ti-ß and Ti-α″ phases.

Microstructure Evolution during Hot Deformation of UNS S32750 Super-Duplex Stainless Steel Alloy.

The present paper analyzes UNS S32750 Super-Duplex Stainless Steel hot deformation behavior during processing by upsetting. The objective of this paper is to determine the optimum range of deformation temperatures, considering that both austenite and ferrite have different deformation behaviors due to their different morphology, physical, and mechanical properties. Because the capability of plastic deformation accommodation of ferrite is reduced when compared to austenite, side cracks and fissures can form during the hot deformation process. Consequently, it is important to find the optimum conditions of deformation of this type of stainless steel to establish the best processing parameters without deteriorating the material. The experimental program involved the application of hot deformation by the upsetting method on a series of samples between 1000 °C and 1275 °C, with a total degree of deformation of 30%. The resultant samples were examined by SEM-EBSD to establish and analyze the evolution of the phases present in the structure from several points of view: nature, distribution, morphology (size and shape), and their structural homogeneity. The GROD (Grain Reference Orientation Deviation) distribution map was also determined while taking into account the possible precipitation of the secondary austenite phase (γ2-phase) and the analysis of the dynamic recrystallization process according to the applied deformation temperature. The main conclusion was that UNS S32750 SDSS steel can be safely deformed by upsetting between 1050-1275 °C, with an experimented total degree of deformation of 30%.