ABSTRACT
(Li2O)0.20(SrO)0.30(Nd2O3)0.01(B2O3)0.49-x(Gd2O3)x, where x = 0, 3, 5, 7, and 10 mol%, glass was melt-quenched to test it as a laser source in the near-infrared (NIR) region. The structural modification, absorption spectra, Judd-Ofelt (J-O) parameters, luminescence spectra, radiative laser parameters, lifetimes, XRD, and FTIR spectra were studied. Luminescence spectra excited at λexc = 584 nm revealed the highest intensity peak at 1073 nm due to the transition of 4F3/2 â 4I11/2. An important phenomenon of concentration quenching was observed and optimized luminescence was achieved with the sample having the concentration x = 07 mol%. The lifetimes of the donor and acceptor and energy transfer from gadolinium to neodymium were obtained from the luminescence decay kinetics. The findings show that Nd-doped Gd2O3-modified glass materials have potential as NIR laser sources.