ABSTRACT
STATEMENT OF PROBLEM: High-speed sintering allows the rapid fabrication of esthetic restorations with adequate flexural strength. However, data on the fatigue behavior of high-speed sintered 4 mol% yttria-stabilized tetragonal zirconia polycrystal (4Y-TZP) are lacking. PURPOSE: The purpose of this in vitro study was to examine the effect of high-speed sintering and the preshading of blanks (monochrome versus multilayer) on the fatigue behavior of 4Y-TZP ceramics. MATERIAL AND METHODS: Four-point flexural strength specimens (N=405) were fabricated from high-speed sintered multilayer 4Y-TZP (Zolid DRS) processed at 1580 °C for about 20 minutes and conventionally sintered at 1450 °C for about 10 hours, multilayer 4Y-TZP (Zolid Gen-x), and monochrome 4Y-TZP (Ceramill Zolid HT+PS), the control group. The specimens were loaded under 5 different dynamic test conditions for fatigue testing (P1-P5). Three were step-stress protocols (P1: 50 N for 5000 cycles; P2: 10 N for 1000 cycles, P3: 5% for 5000 cycles), 1 was tested with a constant force of 720 N (P4), and 1 was tested for different constant load levels (P5). For analysis of P1-P3, the Kaplan-Meier test and Mantel Cox test were performed (α=.05). P4 was analyzed with the Kolmogorov-Smirnov, Kruskal-Wallis, and Mann-Whitney U tests, and P5 by creating a load-cycle diagram. A fracture analysis was performed. RESULTS: ZMLC showed better fatigue behavior than ZMLH (P≤.006) and ZMOC (P≤.002) in all 3 step-stress protocols (P1-P3). ZMLH showed results comparable with those for ZMOC (P≥.285). In P4 and P5, all materials showed comparable values (P=.163 for P4). CONCLUSIONS: The multilayer technique showed a positive effect on the fatigue behavior of 4Y-TZP. In contrast, high-speed sintering negatively influenced the fatigue behavior of multilayer 4Y-TZP. The high-speed sintered material showed no deterioration compared with the conventional sintered monochrome material.
ABSTRACT
PURPOSE: To investigate the impact of high-speed sintering on the accuracy (trueness and reproducibility) and fit of 4Y-TZP full-coverage single-unit fixed dental prostheses (FDPs) and three-unit FDPs. MATERIALS AND METHODS: Single-unit FDPs, conventional three-unit FDPs, and cantilever three-unit FDPs (N = 108; n = 12 per subgroup) were fabricated from: (1) high-speed sintered (1,580°C, about 20 minutes) multi-layer 4Y-TZP (Zolid RS, Amann Girrbach; ZMLH group), as well as two conventionally sintered (1,450°C, about 10 hours) materials: (2) multi-layer 4Y-TZP (Zolid Gen-X, Amann Girrbach; ZMLC group) and (3) monochrome 4Y-TZP (Ceramill Zolid HT+ PS, Amann Girrbach; ZMOC group). All specimens were scanned. Trueness, reproducibility, and fit were measured with 3D analysis software. For data analysis, Kolmogorov-Smirnov, Kruskal-Wallis, and Mann-Whitney U tests were performed (α = .05). RESULTS: Three-unit FDPs made from ZMLH presented a deterioration of accuracy in comparison to ZMLC (P ≤ .001 to .008). The influence of highspeed sintering on marginal and general fit was not clinically relevant (P = .154 to .877). CONCLUSION: High-speed sintering influenced the accuracy of 4Y-TZP full-coverage single-unit and three-unit FDPs. However, no clinically relevant impact on fit was observed.