ABSTRACT
Due to its excellency and versatility, many synthesis methods and conditions were developed to produce HKUST-1 ([Cu3(BTC)2(H2O)3]n). However, the diversity of HKUST-1 was actually generated both in terms of characteristics and morphologies. Hence, the consistency of HKUST-1 characteristics and morphologies needs to be maintained. The statistical analysis and optimization provide features to determine the best synthesis condition. Here, a room-temperature coordination modulation method was proposed to maintain the morphology of HKUST-1 while reducing energy consumption. In addition, response surface methodology (RSM) was used to demonstrate the statistical analysis and optimization of the synthesis of HKUST-1. The molar ratio of ligand to metal, reaction time, and acetic acid concentration were studied to determine their effects on HKUST-1. The optimum HKUST-1 was obtained by the synthesis with a molar ratio of ligand to metal of 0.4703 for 27.2 h using 5% v/v acetic acid concentration. The statistical analysis performed a good agreement with the experimental data and showed the significance of three desired parameters on HKUST-1. The optimum HKUST-1 had the adsorption capacity of 1005.22 mg/g with a removal efficiency of 92.31% towards CV dye. It could be reused up to 5 cycles with insignificant decrease in performance.
ABSTRACT
Due to its excellent characteristics, zeolitic imidazole framework-L (ZIF-L) is widely used in various applications, such as drug delivery, wastewater treatments and energy storage. In the synthesis of ZIF-L, the molar ratio of ligand to metal, the reaction time and the temperature are essential parameters to produce excellent ZIF-L. In this work, ZIF-L was synthesized using a facile and green synthesis method. It was statistically investigated and optimized to obtain the best operating conditions. The optimization was carried out toward the amount of adsorbed crystal violet (CV) dye (q) as the response in the statistics. The optimal ZIF-L was obtained using a molar ratio of ligand to metal of 8.2220 for 97 min at 29 °C, where the q value of the CV adsorption onto this optimal ZIF-L reached 823.02 mg/g. The obtained ZIF-L was characterized using SEM, XRD, FTIR and TGA analyses to ensure its excellent characteristics.
ABSTRACT
Because of their hydrophilic tendencies, the modification of cellulose nanocrystals (CNCs) is needed for applying them as a hydrophobic drug carrier. Previous studies have investigated several modification agents, such as cetyltrimethylammonium bromide. Natural surfactants, such as rarasaponins (RSs), are suitable to avoid human health and environmental issues. In this work, RSs were attached onto CNCs from bamboo shoots to enhance their hydrophobicity. The initial RS concentration and the operating temperature were studied to obtain the best conditions for the modification process, which had significances (p-value < 5%) toward the amount of RSs linked on the CNCs (q) as the response. A q as high as 203.81 ± 0.98 mg/g was obtained at an initial RS concentration of 2000 mg/L and an operating temperature of 30 °C. The curcumin uptake on CNCs-RSs reached 12.40 ± 0.24%, while it was slowly released until approximately 78% in 3 days.
ABSTRACT
Cellulose-based advanced materials, such as cellulose nanocrystals (CNC), have high potential application for drug delivery system. In this study, the CNC were produced from bamboo shoots using acid hydrolysis process. The delignification of bamboo shoots was conducted using alkali and hydrogen peroxide pretreatment processes. The operating condition of the production of CNC from bamboo shoots was optimized using Response Surface Methodology (RSM) based on the yield and crystals recovery as the responses. The optimum CNC yield of 50.67 ± 0.74% with a crystals recovery of 77.99 ± 1.14% was obtained at the sulfuric acid concentration of 54.73 wt% and a temperature of 39 °C from the optimization based on the yield. This optimization has been validated to confirm the accuracy.