Investigation of the Effects of Rapid Thermal Annealing on the Electron Transport Mechanism in Nitrogen-Doped ZnO Thin Films Grown by RF Magnetron Sputtering.

Nitrogen-doped ZnO (ZnO:N) thin films, deposited on Si(100) substrates by RF magnetron sputtering in a gas mixture of argon, oxygen, and nitrogen at different ratios followed by Rapid Thermal Annealing (RTA) at 400 °C and 550 °C, were studied in the present work. Raman and photoluminescence spectroscopic analyses showed that introduction of N into the ZnO matrix generated defects related to oxygen and zinc vacancies and interstitials. These defects were deep levels which contributed to the electron transport properties of the ZnO:N films, studied by analyzing the current-voltage characteristics of metal-insulator-semiconductor structures with ZnO:N films, measured at 298 and 77 K. At the appliedtechnological conditions of deposition and subsequent RTA at 400 °C n-type ZnO:N films were formed, while RTA at 550 °C transformed the n-ZnO:N films to p-ZnO:N ones. The charge transport in both types of ZnO:N films was carried out via deep levels in the ZnO energy gap. The density of the deep levels was in the order of 1019 cm-3. In the temperature range of 77-298 K, the electron transport mechanism in the ZnO:N films was predominantly intertrap tunneling, but thermally activated hopping also took place.

Effect of annealing on the properties of indium-tin-oxynitride films as ohmic contacts for gan-based optoelectronic devices.

Indium-tin-oxynitride (ITON) films have been fabricated by rf sputtering from an indium-tin-oxide target in nitrogen plasma. The influence of postdeposition annealing up to 800 degrees C is analyzed by electrical, optical, and surface characterization of the films in comparison to indium-tin-oxide (ITO) films fabricated in argon plasma. High-temperature annealing resulted in ITO(N) films with similar carrier concentrations. However, the resistivity and optical transmittance of the ITON films were higher than those of the ITO films. Photoelectron spectroscopy revealed that nitrogen is incorporated into the ITON structure in an unbound state as well as through the formation of metal-nitrogen and oxynitride bonds that decorate oxygen vacancies. When the core level electron spectra of ITO and ITON films are compared, a correlation between carrier concentration and the incorporated nitrogen is found. Changes in ITON electrical properties are mainly induced by the release of nitrogen at temperatures above 550 degrees C. In this context, ohmic contact behavior was achieved for ITON on p-type GaN after annealing at 600 degrees C, while no ohmic contact could be realized using ITO.