ABSTRACT
Mn11Ta4O21 is presented as the first hexagonal A-site manganite. Based on simple rules, the structure is compatible with a 14H-layer (cchchch)2 stacking sequence that is related to BaVO3 and BaCrO3 high-pressure polymorphs. The A-site overstoichiometry is explained through difference in ionic radii sizes between Ba and Mn. Magnetic properties show two transitions at TN1 = 88 K and TN2 = 56 K. Neutron powder diffraction evidence two magnetic structures with purely antiferromagnetic and ferrimagnetic orders below TN1 and TN2, respectively. A complementary description with 14H-(hhccccc)2 sequence of only Mn octahedra provides a direct comparison with BaMnO3-δ hexagonal perovskites and naturally explains the AFM order. Below TN2 a magneto-elastic coupling along with uniaxial negative thermal expansion are observed.