Influência de diferentes protocolos de cimentação na resistência de união de pinos de fibra à dentina radicular / Influence of different luting protocols on the bond strength of fiber posts to root dentin

Objetivo: Avaliar a influência de diferentes protocolos de cimentação na resistência de união ao push-out de pinos de fibra cimentados adesivamente à dentina radicular bovina. Método: Os canais de 40 dentes bovinos (comprimento: 16 mm) foram preparados (profundidade: 12 mm) utilizando brocas de preparo (Nº 3, RTD). Cada canal teve sua região apical (4 mm comprimento) incluídas em resina acrílica e as raízes foram divididas em quatro grupos, de acordo com os procedimentos de cimentação(n=10): G1-sistema adesivo de frascos múltiplos com condicionamento total + pino de fibra nº 3; G2-sistema adesivo de frascos múltiplos com condicionamento total + pino de fibra nº 1; G3-sistema adesivo de frascos múltiplos com condicionamento total + pino de fibra no1 + pinos de fibra acessórios; G4-Pinos de fibra nº 3 sem condicionamento total nem procedimentos de união na dentina. Com exceção do grupo G4, a dentina radicular foi tratada com sistema adesivo de frascos múltiplos com condicionamento total (All Bond 2/Bisco). O sistema adesivo foi aplicado utilizando microbrush (Dentsply) e o excesso do material foi removido com pontas de papel absorventes. Os pinos de fibra de quartzo (Macro-Lock Illusion/RTD) foram cimentados à dentina radicular utilizando um cimento resinoso dual (Duolink/Bisco) e, em seguida, foram armazenados em água destilada previamente ao teste mecânico (24 h, 37°C). Cada espécime foi cortada em quatro fatias (1,8 mm de espessura), as quais foram submetidas ao ensaio de push-out em máquina de ensaio universal (1mm/min). Os dados (MPa) foram analisados estatisticamente pela análise de variância (ANOVA-1 fator)...

Resultados: Os valores médios (±DP) obtidos após o ensaio de push-outforam: G1- 5,4±1,3 MPa; G2- 4,2±2,4 MPa; G3-4,6±1,5 MPa; G4-3,3±1,7 MPa. Anova demonstrou não haver significância estatística entre os grupos (p=0,0966). A hipótese foi rejeitada. Conclusão: A resistência de união de pinos de fibra à dentina radicular não foi influenciada pelos protocolos de cimentação avaliados...

Objective: To evaluate the influence of different luting protocols on the push-out bond strength of fiber posts cemented to bovine root dentin. Method: Forty bovine root canals (length: 16 mm) were prepared up to 12 mm using #3 (RTD) preparation burs. Each canal had its apical 4 mm embedded in acrylic resin and the roots were assigned to four groups (n=10), according to the cementation procedures: G1: etch-and-rinse multi-bottle adhesive system + #3 fiber post; G2: etch-and-rinse multibottle adhesive system + #1 fiber post; G3: etch-and-rinse multi-bottle adhesive system + #1 fiber post + accessory fiber posts; G4: #3 fiber post without etching and bonding procedures to dentin. Except for G4, root dentin was treated with the etch-and-rinse multi-bottle adhesive system All Bond 2 (Bisco). The adhesive system was applied with a microbrush (Dentsply) and excess material was removed withabsorbent paper points. The quartz fiber posts (Macro-Lock Illusion/RTD) were cemented to the root dentin with a dual-cure resin cement (Duolink/Bisco) and were stored in distilled water (for 24 h at 37 °C) before the mechanical tests. Each sample was cut into four slices (1.8 mm thick) that were subjected to push-out tests in a universaltesting machine (1 mm/min). The data (in MPa) were analyzed statistically by one-way ANOVA. Results: The mean push-out bond strength values (±SD) were: G1: 5.4 ± 1.3 MPa; G2: 4.2 ± 2.4 MPa; G3: 4.6 ± 1.5 MPa and G4: 3.3 ± 1.7 MPa. One-way ANOVA showed no statistically significant differences among the groups. The tested hypothesis was discarded. Conclusion: The push-out bond strength of fiber posts to root dentin was not influenced by the evaluated luting protocols...

Effect of acid neutralization and mechanical cycling on the microtensile bond strength of glass-ceramic inlays.

OBJECTIVES: To evaluate the hypothesis that a process of hydrofluoric acid precipitate neutralization and fatigue load cycling performed on human premolars restored with ceramic inlays had an influence on microtensile bond strength results (MTBS). METHODS: MOD inlay preparations were performed in 40 premolars (with their roots embedded in acrylic resin). Forty ceramic restorations were prepared using glass-ceramic (IPS Empress). The inner surfaces of all the restorations were etched with 10% hydrofluoric acid for 60 seconds, rinsed with water and dried. The specimens were divided into two groups

Estudo da retenção entre dentes artificiais e resinas acrílicas para base de dentadura ativadas termicamente e por microondas / Study of the adhesion between artificial teeth and acrylic resin of denture base using thermal conventional activation and microwaves

O intuito deste trabalho foi verificar a resistência de união entre dentes artificiais acrílicos e resinas acrílicas para base de dentadura. Ensaios de tração foram realizados utilizando dois tipos de dentes: Biotone (Dentsply) e Orthosit (Ivoclar); e dois tipos de resinas para base: polimerizada por microondas (Onda Cryll) e termicamente ativada, de maneira tradicional (Clássico). Comparou-se também o pincelamento ou não da superfície dos dentes artificiais com monômero, antes da prensagem, como alternativa para melhorar a adesão. Conclui-se que houve diferença na resistência de união entre os tipos de dentes testados, independente do tipo de resina para base. Os diferentes modos de ativação das resinas para base não proporcionaram diferença na resistência de união. O pincelamento de monômero na superfície dos dentes, antes da inclusão, aumentou a adesão à resina, principalmente para os dentes da marca Orthosit. Os melhores resultados foram conseguidos com os dentes da marca Biotone, quando processados por banho de água quente e com a superfície pincelada com monômero antes da inclusão