ABSTRACT
One of the most commonly applied methods of joining dissimilar materials is gluing. This could be mainly attributed to the applicability of this technique in various industries. The article presents a method of material surface treatment, which increases the shear strength of adhesive joints for lightweight metals such as aluminum with plastics. For this purpose, laser surface microstructuring was performed on each of the selected construction materials. As a result of the performed treatment, the active surface of the glued area was increased, which increased the adhesive strength. The picosecond laser with UV radiation used in the research is TruMicro 5325c with which material can be removed as a result of the cold ablation phenomenon. The applied parameters of the laser device did not cause thermal damage to the surface of the microstructured materials, which was confirmed by microscopic examination. Laser micromachining did not deteriorate the degree of wetting of the tested materials, either, as was confirmed by the contact angle and surface energy measurements with the use of water as the measuring liquid. In investigated cases of microstructure types, the presented method significantly increased the shear strength of the joints formed, as demonstrated by the presented strength test results. Research has shown that created joints with microstructure made according to the described method, are characterized by a significant increase in strength, up to 376%, compared to materials without microstructure. The presented results are part of a series of tests aimed at selecting the operating laser parameters for the implementation of geometric shapes of microstructures which will increase the strength of adhesive joints in selected materials.
ABSTRACT
The study aimed at investigating the microstructure and mechanical properties of Neodymium-Doped Yttrium Aluminum Garnet (Nd:YAG) laser welded high strength low alloy (HSLA) SA516 grade 70 boiler steel. The weld joint for a 4 mm thick plate was successfully produced using minimum laser power of 2 kW by employing a single pass without any weld preheat treatment. The micrographs revealed the presence of martensite phase in the weld fusion zone which could be due to faster cooling rate of the laser weldment. A good correlation was found between the microstructural features of the weld joints and their mechanical properties. The highest hardness was found to be in the fusion zone of cap region due to formation of martensite and also enrichment of carbon. The hardness results also showed a narrow soft zone at the heat affected zone (HAZ) adjacent to the weld interface, which has no effect on the weld tensile strength. The yield strength and ultimate tensile strength of the welded joints were 338 MPa and 549 MPa, respectively, which were higher than the candidate metal. These tensile results suggested that the laser welding process had improved the weld strength even without any weld preheat treatment and also the fractography of the tensile fractured samples showed the ductile mode of failure.