Polyimide biocomposites coated with tantalum pentoxide for stimulation of cell compatibility and enhancement of biointegration for orthopedic implant.

Orthopedic implants are an important tool in the treatment of musculoskeletal conditions and helped many patients to improve their quality of life. Various inorganic-organic biocomposites have been broadly investigated particularly in the area of load-bearing orthopedic/dental applications. Polyimide (PI) is a promising organic material and shows excellent mechanical properties, biocompatibility, bio-stability, and its elastic modulus is similar to human bone but it lacks bioactivity, which is very important for cell adhesion and ultimately for bone regeneration. In this research, tantalum pentoxide (Ta2O5) coating was prepared on the surface of PI by polydopamine (PDA) bonding. The results showed that Ta2O5 was evenly coated on the surface of PI, and with the concentration of Ta2O5 in the PDA suspension increased, the content of Ta2O5 particles on the surface of PI increased significantly. In addition, the Ta2O5 coating significantly increased the roughness and hydrophilicity of the PI matrix. Cell experiments showed that PI surface coating Ta2O5 could promote the proliferation, adhesion, and osteogenic differentiation of bone marrow-derived stromal cells (BMSCs). The results demonstrated that fabricating Ta2O5 coating on the surface of PI through PDA bonding could improve the biocompatibility as well as bioactivity of PI, and increase the application potential of PI in the field of bone repair materials.

Tantalum oxide submicro-particles into microporous coating on polyimide possessing antibacterial property and inducing cellular response for orthopedic application.

Surface characteristics of the biomaterials have significant effects on response of osteoblast and formation of new bone tissue. In this study, to improve the bio-performance of polyimide (PI) as an implantable material for bone substitute, concentrated sulfuric acid suspension with tantalum (V) oxide (vTO) submicro-particles of 10w% (PIST10) and 15w% (PIST15) was utilized to modify PI surface. After sulfonation, microporous coatings including vTO particles were created on PI (PIST10 and PIST15) while microporous coating without vTO particles was also created on PI (PIS). Results showed that surface roughness, hydrophilicity and protein adsorption of PIST15 was remarkably higher than PIST10 and PIS. Furthermore, after soaking into simulated body fluid (SBF), no apatite mineralization on PIS was found, while PIST15 with high vTO content exhibited better apatite mineralization compared with PIST10. Moreover, PIS showed low antibacterial property, while PIST15 with high vTO content revealed better antibacterial property compared with PIST10. In addition, cellular response (such as adhesion, proliferation and alkaline phosphatase activity) of bone marrow stromal cells (BMSC) of rat to PIST15 was higher than PIST10 and PIS. In conclusion, the microporous coating of PIST15 including vTO submicro-particles possessed good antibacterial property and bioactivity, which significantly promoted the responses of BMSC. Therefore, PIST15 has potential application prospects for bone substitute.