Downshift of the Ni d band center over Ni nanoparticles in situ confined within an amorphous silicon nitride matrix.

Herein, nanocomposites made of Ni nanoparticles in situ distributed in an amorphous silicon nitride (Ni/a-Si3N4) matrix, on the one hand, and within an amorphous silicon dioxide (Ni/a-SiO2) matrix, on the other hand, were synthesized from the same Ni-modified polysilazane precursor. In both compounds, the Ni/Si atomic ratio (0.06-0.07), average Ni nanocrystallite size (7.0-7.6 nm) and micro/mesoporosity of the matrix were rigorously fixed. Hydrogen (H2)-temperature-programmed desorption (TPD) profile analysis revealed that the activation energy for H2 desorption at about 100-130 °C evaluated for the Ni/a-Si3N4 sample (47.4 kJ mol-1) was lower than that for the Ni/a-SiO2 sample (68.0 kJ mol-1). Mechanistic study with X-ray photoelectron spectroscopy (XPS) analysis and density functional theory (DFT) calculations revealed that, at Ni nanoparticle/matrix heterointerfaces, Ni becomes more covalently bonded to N atoms in the a-Si3N4 matrix compared to O atoms in the a-SiO2 matrix. Therefore, based on experimental and theoretical studies, we elucidated that nickel-nitrogen (Ni-N) interactions at the heterointerface lead to remarkable Ni d band broadening and downshifting of the d band center relative to those generated by Ni-oxygen (Ni-O) interactions at the heterointerface. This facilitates H2 desorption, as experimentally observed in the Ni/a-Si3N4 sample.

Mechanistic Investigation of the Formation of Nickel Nanocrystallites Embedded in Amorphous Silicon Nitride Nanocomposites.

Herein, we report the mechanistic investigation of the formation of nickel (Ni) nanocrystallites during the formation of amorphous silicon nitride at a temperature as low as 400 °C, using perhydropolysilazane (PHPS) as a preformed precursor and further coordinated by nickel chloride (NiCl2); thus, forming the non-noble transition metal (TM) as a potential catalyst and the support in an one-step process. It was demonstrated that NiCl2 catalyzed dehydrocoupling reactions between Si-H and N-H bonds in PHPS to afford ternary silylamino groups, which resulted in the formation of a nanocomposite precursor via complex formation: Ni(II) cation of NiCl2 coordinated the ternary silylamino ligands formed in situ. By monitoring intrinsic chemical reactions during the precursor pyrolysis under inert gas atmosphere, it was revealed that the Ni-N bond formed by a nucleophilic attack of the N atom on the Ni(II) cation center, followed by Ni nucleation below 300 °C, which was promoted by the decomposition of Ni nitride species. The latter was facilitated under the hydrogen-containing atmosphere generated by the NiCl2-catalyzed dehydrocoupling reaction. The increase of the temperature to 400 °C led to the formation of a covalently-bonded amorphous Si3N4 matrix surrounding Ni nanocrystallites.

Low temperature in situ formation of cobalt in silicon nitride toward functional nitride nanocomposites.

This work highlights the first demonstration of a low-temperature in situ formation of Co nanocrystallites embedded within an amorphous silicon nitride matrix through careful control of the chemistry behind material design using perhydropolysilazane (PHPS) as a Si3N4 precursor further coordinated with CoCl2 and ammonia as a pyrolysis atmosphere. The Co nucleation was allowed to proceed at temperatures as low as 400 °C via thermal decomposition of Co2N pre-formed in situ by the reaction of CoCl2 with the Si centers of PHPS at the early stage of pyrolysis (220-350 °C).