ABSTRACT
The objective of this study was to analyze the physico-mechanical properties of gypsum boards including plastic waste aggregates from cable recycling. The plastic cable waste is incorporated into the gypsum matrix without going through any type of selection and/or treatment, as it is obtained after the cable recycling process. In the experimental process, gypsum boards of different dimensions were manufactured and tested for their Young's modulus, shock-impact resistance, flexural strength, thermal conductivity, and thermal comfort. The results obtained show a significant increase in the elasticity of the boards with plastic waste (limited cracking), compliance with the minimum value of flexural strength, and a slight improvement in the thermal conductivity coefficient (lower energy demand) and surface comfort (reduced condensation and greater adherence). Therefore, the analyzed material could provide a suitable alternative to currently marketed gypsum boards, contributing to sustainable construction not only in new constructions, but also in building renovations.
ABSTRACT
This paper shows the characterization of a new lightened gypsum-based material for use in buildings. A plaster material has been designed with a polymeric compound based on polyvinyl acetate, bicarbonate and a boric acid solution, which reduce the density and thermal conductivity by up to 20% and 30%, respectively. In addition, tests have been carried out with the lightened plaster material reinforced with glass (GF), basalt (BF), polypropylene (PPF) and wood (WF) fibers. A significant improvement in mechanical properties was achieved. All samples obtained resistance values greater than 2 MPa in flexion and 3 MPa in compression. Physico-chemical analysis were also carried out. The study is completed with a statistical analysis, where confidence intervals have been obtained for the mean at 95% confidence for each of the physical properties studied.
ABSTRACT
Non-destructive testing can be used to determine some of the most relevant physical properties of building materials. In this work, two low-cost measuring devices were developed capable of determining the variation in real-time of the percentage of humidity that is produced in the construction of gypsum and plaster during the hardening process. For this, an Arduino resistive sensor and a capacitive sensor of our design were used. The results show how it is possible to determine the variations in mixing water content during the seven days of curing established by the UNE-EN 13279-2 standard as well relate to the mechanical resistance of the test specimens with the same percentage of humidity. Additionally, the study was completed with the determination of the formation of the dihydrate compound linked to this setting process in the test specimens by conducting X-ray diffraction and thermogravimetric analysis tests at different ages of the samples.