Effect of sulfur doping of zinc-imidazole coordination polymer (ZnIm CP) as a novel photocatalyst for degradation of ionic dyes.

Zinc-Imidazole coordination polymer (ZnImCP) was simply synthesized hydrothermally at relatively low temperature (70 °C) from zinc acetate and imidazole. ZnImCP was treated by sulfide solution to produce sulfur-doped samples (S-ZnImCPs). Structures of the synthesized ZnImCP and S-ZnImCPs were characterized through FTIR, PXRD, and, Raman, SEM/EDX, N2-BET, UV-VIS DRS, and pHpzc analyses. The photocatalytic performances of pristine CP and sulfur modified CPs under visible and ultra-violet irradiations for degrading the cationic methylene blue (MB) and the anionic methyl orange (MO) were investigated considering different initial pH values 4, 7 and 10. Under visible light, the results indicate that these CPs display considerable photocatalytic degradation towards the cationic MB for the initial pH 4 and 7 where degradation increases with sulfur content. While under ultra-violet, results indicate considerable photocatalytic degradation towards both dyes for the initial pH 7 and 10 where degradation increases with sulfur content which indicates the gainful of non-metal dopping. The buffering nature of CPs and the type of radiation considering determined band-gap values effectively influence the degradation mechanisms.

Leptin improves the in vitro development of preimplantation rabbit embryos under oxidative stress of cryopreservation.

Vitrification is an economically effective method for embryo cryopreservation in human and livestock animals; however, it carries the risk of damage by the exposure to severe oxidative stress. The present study was conducted to evaluate the effect of leptin at different levels on the in vitro development of fresh and vitrified preimplantation embryos in a rabbit model. Normal embryos at morulae stage were randomly cultured for 2 h with 0, 10, 20 or 100 ng/mL of leptin, then were cultured for further 48 h as freshly or after vitrification. Thereafter, developed blastocysts form the best leptin level in fresh and vitrified embryos along with their controls were allocated to analyze the pro-oxidant (malondialdehyde, MDA; nitric oxide, NO), antioxidant (total antioxidant capacity, TAC; superoxide dismutase, SOD; glutathione peroxidase, GPx), apoptotic (Bcl-2 associated X protein, BAX; heat shock 60kD protein member 1, HSP60; tumor necrosis factor alpha, TNFα) and developmental (sex determining region Y box protein 2, SOX2; Nanog homeobox protein, NANOG; Octamer-binding protein 4, OCT4) biomarkers. Results indicate that expanding and hatching rates of embryos were significantly higher at 20 ng/mL leptin than the other levels, while vitrification had an independent suppression effect on the in vitro development rates. The MDA and NO were significantly higher, while TAC, SOD and GPx were significantly lower in the vitrified than fresh embryos. In contrast, leptin treatment significantly decreased the pro-oxidant biomarkers and increased the antioxidant biomarkers in both fresh and vitrified embryos. Vitrification significantly increased the antiapoptotic biomarkers, and decreased the developmental biomarkers in embryos. In contrast, leptin decreased the BAX and TNFα, increased the HSP60, and moreover, ameliorated the reduction of developmental biomarkers in the vitrified embryos. These results conclude that leptin could be used as antiapoptotic and antioxidant promotor to support the in vitro embryonic development, particularly under oxidative stress emerged from cryopreservation programs.

Novel porous Al2O3-SiO2-TiO2 bone grafting materials: formation and characterization.

The present article deals with the development of 3D porous scaffolds for bone grafting. They were prepared based on rapid fluid infiltration of Al2O3-SiO2 sol into a polyethylene non-woven fabric template structure. Titanium dioxide in concentration equal to 5 wt% was added to the Al2O3-SiO2 mixture to produce Al2O3-SiO2-TiO2 composite scaffolds. The prepared scaffolds are characterized by means of X-ray diffraction, scanning electron microscopy and three-point bending test techniques. The bioactivity of the produced bodies is discussed, including the in vitro and in vivo assessments. The produced scaffolds exhibit mean total porosity of 66.0% and three-point bending strength of 7.1 MPa. In vitro studies showed that MG-63 osteoblast-like cells attach and spread on the scaffolds surfaces. Furthermore, cells grew through the scaffolds and start to produce extra-cellular matrix. Additionally, in vivo studies revealed the ability of the porous scaffolds to regenerate bone tissue in femur defects of albino rats 5 months post surgery. Histological analysis showed that the defect is almost entirely filled with new bone. The formed bone is characterized as a mature bone. The produced bone grafts are intended to be used as bone substitute or bone filler as their degradation products caused no inflammatory effects.

Synthesis and characterization of laminated Si/SiC composites.

Laminated Si/SiC ceramics were synthesized from porous preforms of biogenous carbon impregnated with Si slurry at a temperature of 1500 °C for 2 h. Due to the capillarity infiltration with Si, both intrinsic micro- and macrostructure in the carbon preform were retained within the final ceramics. The SEM micrographs indicate that the final material exhibits a distinguished laminar structure with successive Si/SiC layers. The produced composites show weight gain of ≈5% after heat treatment in air at 1300 °C for 50 h. The produced bodies could be used as high temperature gas filters as indicated from the permeability results.