1.
Surf Coat Technol ; 4142021 May 25.
Article in English | MEDLINE | ID: mdl-34966191

ABSTRACT

Electrolytic plasma processing (EPP) was used to create hydrophilic surface profiles on titanium. The wettability, surface morphology characteristics and chemical composition of the treated samples were studied as a function of EPP processing parameters. The EPP profiled surfaces comprised of a characteristic "hills and valleys" morphology because of continuous surface melting and freezing cycles. A bimodal surface profile was produced with 2-3 µm height hills and valleys with nano-roughness (≤200 nm). The produced profile resulted in a significant contact angle decrease (from 38.7° to 5.4°). Ratios of actual surface area to projection area (r) and fraction of solid surface remaining dry (φ) were obtained from profilometry. The surface characteristics and large r values produced by EPP were able to induce hemi-wicking. Hence, EPP produced superhydrophilic surfaces on Ti. The bioactivity of EPP treated Ti was evaluated using cell free and MC3T3 cells in-vitro studies. The treated Ti surface significantly increased the bioactivity and formed stoichiometric hydroxyapatite after immersion in a bone cell culture medium for 21 days. Cells' attachment and proliferation studies indicated that EPP treated surface significantly enhances the cells' adhesion and growth after 24 and 48 h compared to the untreated surface. The results show that Ti surface profiling by EPP constitutes a promising method to potentially improve bone implant bonding.

2.
JBMR Plus ; 5(4): e10425, 2021 Apr.
Article in English | MEDLINE | ID: mdl-33869985

ABSTRACT

Critical-sized bone defects are challenging to heal because of the sudden and large volume of lost bone. Fixative plates are often used to stabilize defects, yet oxidative stress and delayed angiogenesis are contributing factors to poor biocompatibility and delayed bone healing. This study tests the angiogenic and antioxidant properties of amorphous silicon oxynitrophosphide (SiONPx) nanoscale-coating material on endothelial cells to regenerate vascular tissue in vitro and in bone defects. in vitro studies evaluate the effect of silicon oxynitride (SiONx) and two different SiONPx compositions on human endothelial cells exposed to ROS (eg, hydrogen peroxide) that simulates oxidative stress conditions. in vivo studies using adult male Sprague Dawley rats (approximately 450 g) were performed to compare a bare plate, a SiONPx-coated implant plate, and a sham control group using a rat standard-sized calvarial defect. Results from this study showed that plates coated with SiONPx significantly reduced cell death, and enhanced vascular tubule formation and matrix deposition by upregulating angiogenic and antioxidant expression (eg, vascular endothelial growth factor A, angiopoetin-1, superoxide dismutase 1, nuclear factor erythroid 2-related factor 2, and catalase 1). Moreover, endothelial cell markers (CD31) showed a significant tubular structure in the SiONPx coating group compared with an empty and uncoated plate group. This reveals that atomic doping of phosphate into the nanoscale coating of SiONx produced markedly elevated levels of antioxidant and angiogenic markers that enhance vascular tissue regeneration. This study found that SiONPx or SiONx nanoscale-coated materials enhance antioxidant expression, angiogenic marker expression, and reduce ROS levels needed for accelerating vascular tissue regeneration. These results further suggest that SiONPx nanoscale coating could be a promising candidate for titanium plate for rapid and enhanced cranial bone-defect healing. © 2020 The Authors. JBMR Plus published by Wiley Periodicals LLC. on behalf of American Society for Bone and Mineral Research.

3.
Med Devices Sens ; 4(1)2021 Feb.
Article in English | MEDLINE | ID: mdl-35765350

ABSTRACT

The current study provides more insights about the surface bioactivity of the silicon nitride (Si3N4) as a potential candidate for bone regeneration in craniofacial and orthopaedic applications compared with conventional implantation materials. Current skeletal reconstructive materials such as titanium and polyether ether ketone (PEEK) are limited by poor long-term stability, biocompatibility and prolonged healing. Si3N4 is an FDA-approved material for an intervertebral spacer in spinal fusion applications. It is biocompatible and has antimicrobial properties. Here, we hypothesize that Si3N4 was found to be an osteoconductive material and conducts the growth, differentiation of MC3T3-E1 cells for extracellular matrix deposition, mineralization and eventual bone regeneration for craniofacial and orthopaedic applications. MC3T3-E1 cells were used to study the osteoblastic differentiation and mineralization on sterile samples of Si3N4, titanium alloy and PEEK. The samples were then analysed for extracellular matrix deposition and mineralization by FTIR, Raman spectroscopy, SEM, EDX, Alizarin Red, qRT-PCR and ELISA. The in vitro study indicates the formation of collagen fibres and mineral deposition on all three sample surfaces. There was more profound and faster ECM deposition and mineralization on Si3N4 surface as compared to titanium and PEEK. The FTIR and Raman spectroscopy show formation of collagen and mineral deposition at 30 days for Si3N4 and titanium and not PEEK. The peaks shown by Raman for Si3N4 resemble closely to natural bone. Results also indicate the upregulation of osteogenic transcription factors such as RUNX2, SP7, collagen type I and osteocalcin. The authors concluded that Si3N4 rapidly conducts mineralized tissue formation via extracellular matrix deposition and biomarker expression in mouse calvarial pre-osteoblast cells. Thus, this study confirms that the bioactive Si3N4 could be a potential material for craniofacial and orthopaedic applications leading to rapid bone regeneration that resemble the natural bone structure.

4.
Tissue Eng Part A ; 26(1-2): 15-27, 2020 01.
Article in English | MEDLINE | ID: mdl-31044666

ABSTRACT

Lack of osteointegration is a major cause of aseptic loosening and failure of implants used in bone replacement. Implants coated with angiogenic biomaterials can improve osteointegration and potentially reduce these complications. Silicon- and phosphorus-based materials have been shown to upregulate expression of angiogenic factors and improve endothelial cell functions. In the present study, we hypothesize that implants coated with amorphous silica-based coatings in the form of silicon oxynitrophosphide (SiONP) by using plasma-enhanced chemical vapor deposition (PECVD) technique could enhance human umbilical vein endothelial cell angiogenic properties in vitro. The tested groups were: glass coverslip (GCS), tissue culture plate, SiON, SiONP1 (O: 7.3 at %), and SiONP2 (O: 14.2 at %) implants. The SiONP2 composition demonstrated 3.5-fold more fibronectin deposition than the GCS (p < 0.001). The SiONP2 group also presented a significant improvement in the capillary tubule length and thickness compared with the other groups (p < 0.01). At 24 h, we observed at least a twofold upregulation of vascular endothelial growth factor A, hypoxia-inducible factor-1α, angiopoietin-1, and nesprin-2, more evident in the SiONP1 and SiONP2 groups. In conclusion, the studied amorphous silica-coated implants, especially the SiONP2 composition, could enhance the endothelial cell angiogenic properties in vitro and may induce faster osteointegration and healing. Impact Statement In this study, we report for the first time the significant enhancement of human umbilical vein endothelial cell angiogenic properties (in vitro) by the amorphous silica-based coatings in the form of silicon oxynitrophosphide (SiONP). The SiONP2 demonstrated 3.5-fold more fibronectin deposition than the glass coverslip and presented a significant improvement in the capillary tubule length and thickness. At 24 h, SiONP reported twofold upregulation of vascular endothelial growth factor A, hypoxia-inducible factor-1α, angiopoietin-1, and nesprin-2. The studied amorphous silica-coated implants enhance the endothelial cell angiogenic properties in vitro and may induce faster osteointegration and healing.


Subject(s)
Biocompatible Materials/pharmacology , Human Umbilical Vein Endothelial Cells/cytology , Human Umbilical Vein Endothelial Cells/drug effects , Silicon Dioxide/chemistry , Angiopoietin-1/metabolism , Cell Proliferation/drug effects , Cell Survival/drug effects , Cells, Cultured , Human Umbilical Vein Endothelial Cells/metabolism , Humans , Hypoxia-Inducible Factor 1, alpha Subunit/metabolism , Microfilament Proteins/metabolism , Nerve Tissue Proteins/metabolism , Reverse Transcriptase Polymerase Chain Reaction , Vascular Endothelial Growth Factor A/metabolism
5.
Water Sci Technol ; 80(2): 377-386, 2019 Jul.
Article in English | MEDLINE | ID: mdl-31537774

ABSTRACT

Sol-gel auto-combustion technique was used to synthesize spinel ferrite nanoparticles of Mn0.2Co0.8Fe2O4 (MCF). Using the modified Stöber method, these magnetic nanoparticles were encapsulated with silica to form the core/shell Mn0.2Co0.8Fe2O4/SiO2 (MCFS). The phase composition, morphology, particle size, and saturation magnetization of the encapsulated nanoparticles were studied using X-ray diffraction (XRD), high resolution-transition electron microscopy (HR-TEM), and vibrating sample magnetometer (VSM). HR-TEM images indicated that particle size of the nanoparticles ranged from 15 to 40 nm, and VSM measurements showed that Ms of uncoated and coated samples were 65.668 emu/g and 61.950 emu/g and the Hc values were 2,151.9 Oe and 2,422.0 Oe, respectively. The effects of metal concentration, solution pH, contact time, and adsorbent dose of the synthesized nanoparticles on lead (Pb2+) ions removal from an aqueous solution were investigated. Based on Langmuir isotherm model, the results for peak adsorption capacity of the adsorbent under optimal conditions was 250.5 mg/g and 247 mg/g for MCF and MCFS, respectively. We concluded that Pb2+ adsorption occurred via a chemisorption mechanism based on the analysis of adsorption kinetics. The adsorbents displayed consistent adsorption efficiencies following three cycles of regeneration, indicating that these magnetic nanoparticles are promising candidates for wastewater purification.


Subject(s)
Magnetite Nanoparticles , Silicon Dioxide , Adsorption , Lead , Magnetics
6.
Med Devices Sens ; 2(2)2019 Apr.
Article in English | MEDLINE | ID: mdl-35781939

ABSTRACT

The bioactive silicon nitride (Si3N4) has been FDA cleared for use as spinal intervertebral arthrodesis devices. Because its surface properties promote bone ongrowth and ingrowth, it also has the potential to benefit craniofacial reconstruction. Thus, the aim of this work was to determine whether the surface properties of Si3N4 could enhance the osteoblast cell growth, differentiation and nucleation of hydroxyapatite (HA) crystals compared to conventional implant materials such as titanium (Ti) and polyether ether ketone (PEEK). X-ray absorbance near-edge structure analysis (XANES) indicated the presence of Si-Si, Si-O and Si-N bonding. Surface wettability studies confirmed that Si3N4 exhibits the lowest contact angle and highest surface energy. Cell culture studies showed that osteoblast growth was enhanced on Si3N4 after 1 day and up to 7 days. Si3N4 surface induced highest surface coverage and thickness of nanocrystalline HA (211) and (203) in cell-free in vitro studies after 7 days of culture. Raman spectroscopy analysis confirmed the presence of surface functional groups consisting of phosphate and carbonate species. Interestingly, Si3N4 surface showed amide and hydroxyproline groups, the precursors to collagen, which were not observed on Ti and PEEK surfaces. Furthermore, Si3N4 surface indicated high expression of RUNX2, enhanced cell differentiation and dense collagenous ECM after 30 days of the in vitro study. The present study concluded that Si3N4 surface enhances osteoprogenitor cell adhesion, growth, RUNX2 expression and ECM formation via the coupled effects of higher surface energy and the presence of amide and nanocrystalline HA functional groups.