ABSTRACT
Due to the sensitivity to water, the all-inorganic CsPbBr3 nanocrystals have been widely applied in information encryption with spatial dimensions. However, the absence of time-dimension information limits the information capacity for the application of CsPbBr3. In this work, the CsPbBr3 nanocrystal was combined with water-sensitive borophosphate glass, achieving decomposing/recrystallization of CsPbBr3 nanocrystal with multi-dimension. The addition of SiO2 confirms that the collapse of the borophosphate glass network structure causes the exposure of the CsPbBr3 nanocrystals. The decomposition and recrystallization mechanism of CsPbBr3 nanocrystals in glass-ceramics upon encountering water has been verified. Finally, an information encryption strategy, using the mixture of CsPbBr3 glass ceramic and sodium carboxymethylcellulose as ink, is designed via adopting screen-printing technology, which not only provides a new idea for the preparation of CsPbBr3 nanocrystals, but also establish a new avenue for the information encryption technology.
ABSTRACT
Epoxy resin adhesive for pavement is often insufficient in flexibility and toughness. Therefore, a new type of toughening agent was prepared to overcome this shortcoming. To achieve the best toughening effect of a self-made toughening agent on an epoxy resin adhesive, its ratio to the epoxy resin needs to be optimally selected. A curing agent, a toughening agent, and an accelerator dosage were chosen as independent variables. The epoxy resin's adhesive tensile strength, elongation at break, flexural strength, and flexural deflection were used as response values to establish a single-objective prediction model of epoxy resin mechanical property indexes. Response surface methodology (RSM) was used to determine the single-objective optimal ratio and analyze the effect of factor interaction on epoxy resin adhesive's performance indexes. Based on principal component analysis (PCA), multi-objective optimization was performed using gray relational analysis (GRA) to construct a second-order regression prediction model between the ratio and gray relational grade (GRG) to determine the optimal ratio and to validate it. The results showed that the multi-objective optimization using response surface methodology and gray relational analysis (RSM-GRA) was more effective than the single-objective optimization model. The optimal ratio of epoxy resin adhesive was 100 parts of epoxy resin, 160.7 parts curing agent, 16.1 parts toughening agent, and 3.0 parts accelerator. The measured tensile strength was 10.75 MPa, elongation at break was 23.54%, the bending strength was 6.16 MPa, and the bending deflection was 7.15 mm. RSM-GRA has excellent accuracy for epoxy resin adhesive ratio optimization and can provide a reference for the epoxy resin system ratio optimization design of complex components.