ABSTRACT
A new maraging stainless steel with superior strength-toughness-corrosion synergy has been developed based on an innovative concept of alloy design. The high strength-toughness combination is achieved by forming dispersive nano-sized intermetallic compounds in the soft lath martensitic matrix with a slight amount of residual austenite. The good corrosion resistance is guaranteed by exactly controlling the Co content based on understanding the synergistic effect between Co and Cr. The fine structure characteristics of two dominant strengthening precipitations including Ni3Ti and Mo-rich phases were finely characterized associated with transmission electron microscope (TEM) and atom probe tomography (APT) analyses. The relationship among microstructure, strength and toughness is discussed. The precipitation mechanism of different precipitates in the new maraging stainless steel is revealed based on the APT analysis.
ABSTRACT
Co-Cr-W-Ni alloy (L605) with high tensile strength is used in coronary stents. The thickness of individual strut of the stent is reduced which can decrease the stent restenosis rate. However, about 10% Ni element content in L605 is found to cause allergic reactions and pulmonary embolism, similar to the traditional 316L stainless steel. In this study, a novel nickel-free cobalt-base alloy Co-20Cr-12Fe-18Mn-2Mo-4W-N (wt%) was designed and fabricated in order to efficiently avoid the potential hazards of Ni element. Fe and Mn, essential elements of human body, were added in the alloy to substitute part of Co element. In comparison to L605 alloy, the tensile strength of the new alloy was higher than 1000MPa while elongation was above 55%. The pitting potential of the new alloy was measured close to 1000mV, also higher than that of L605 alloy. CCK-8 test indicated that the cytotoxicity of the new alloy is grade 1, reflecting that Co-20Cr-12Fe-18Mn-2Mo-4W-N alloy has no cytotoxic effects. There was no significant difference in the apoptosis rates between Co-20Cr-12Fe-18Mn-2Mo-4W-N and L605 alloy. The newly developed cobalt-base alloy showed excellent mechanical, corrosion resistance and biological properties, which could make it a desirable material for future clinical investigations.