ABSTRACT
In this study, the effects of capping layers with different metals on the electrical performance and stability of p-channel SnO thin-film transistors (TFTs) were examined. Ni- or Pt-capped SnO TFTs exhibit a higher field-effect mobility (µFE), a lower subthreshold swing (SS), a positively shifted threshold voltage (VTH), and an improved negative-gate-bias-stress (NGBS) stability, as compared to pristine TFTs. In contrast, Al-capped SnO TFTs exhibit a lower µFE, higher SS, negatively shifted VTH, and degraded NGBS stability, as compared to pristine TFTs. No significant difference was observed between the electrical performance of the Cr-capped SnO TFT and that of the pristine SnO TFT. The obtained results were primarily explained based on the change in the back-channel potential of the SnO TFT that was caused by the difference in work functions between the SnO and various metals. This study shows that capping layers with different metals can be practically employed to modulate the electrical characteristics of p-channel SnO TFTs.
ABSTRACT
We utilized Ni as a floating capping layer in p-channel SnO thin-film transistors (TFTs) to improve their electrical performances. By utilizing the Ni as a floating capping layer, the p-channel SnO TFT showed enhanced mobility as high as 10.5 cm2·V-1·s-1. The increase in mobility was more significant as the length of Ni capping layer increased and the thickness of SnO active layer decreased. The observed phenomenon was possibly attributed to the changed vertical electric field distribution and increased hole concentration in the SnO channel by the floating Ni capping layer. Our experimental results demonstrate that incorporating the floating Ni capping layer on the channel layer is an effective method for increasing the field-effect mobility in p-channel SnO TFTs.