ABSTRACT
The study aimed to understand how changes in crystal's size affect the lattice parameters and crystal structure of Mg1-xNixO solid solution for six X values ranging from x = 0 to x = 1. Mg1-xNixO was synthesized via two different wet-chemical techniques: the sol-gel and the microwave hydrothermal method, both followed by calcination at different temperatures of 673, 873, 1073, 1273 and 1473 K. As annealing caused grain growth, the varied temperature range allowed to examine a wide range of grain sizes. The lattice parameters and x values were determined from XRD (X-ray diffraction) peak positions and intensities respectively. The grain size was evaluated by XRD line profile analysis and supported by SEM (scanning electron microscope) observations. At the temperatures of 673 and 873 K grain size was in the nanometric range and from 1073 K and above grain size was in the micrometric range. A non-monotonic lattice variation versus grain size was found for each concentration. When grain size decreased there was a slight contraction, however for grain size in the nanometric range there was a severe lattice expansion. Both lattice parameter changes were explained by two effects acting together: contraction due to surface stress and expansion due to weakening of the ionic bonding at nanocrystalline particles. In this current research study, the lattice parameter was mapped in two dimensions: concentration and grain size. The findings of this study provided valuable insights into the lattice variation in the MgO-NiO solid solution system.
ABSTRACT
Rare-earth (RE) oxides are important in myriad fields, including metallurgy, catalysis, and ceramics. However, the phase diagram of RE oxides in the nanoscale might differ from the phase diagrams for bulk, thus attracting attention nowadays. We suggest that grain size in the nanoscale also determines the obtained crystallographic phase along with temperature and pressure. For this purpose, nanoparticles of Sm2O3 and Eu2O3 were mixed in an inert MgO matrix via the sol-gel method. This preparation method allowed better isolation of the oxide particles, thus hindering the grain growth process associated with increasing the temperature. The mixed oxides were compared to pure oxides, which were heat-treated using two methods: gradual heating versus direct heating to the phase transition temperature. The cubic phase in pure oxides was preserved to a higher extent in the gradual heating treatment compared to the direct heating treatment. Additionally, in MgO, even a higher extent of the cubic phase was preserved at higher temperatures compared to the pure oxide, which transformed into the monoclinic phase at the same temperature in accordance with the phase diagram for bulk. This indicates that the cubic phase is the equilibrium phase for nanosized particles and is determined also by size.
ABSTRACT
Zirconia (ZrO2) and yttria-stabilized-zirconia (YSZ) are known as advanced oxides, widely applied in gas-turbine engines, fuel cells and other applications, requiring controlled thermal conductivity values. In the current research hot-pressed ZrO2-8YSZ composites, were synthesized. The effect of the three apparent phases, 8YSZ, ZrO2 and the pores on the thermal conductivity was analyzed using the general effective media (GEM) approach, while considering their relative amounts and morphology.
ABSTRACT
Porous yttria-stabilised zirconia ceramics have been gaining popularity throughout the years in various fields, such as energy, environment, medicine, etc. Although yttria-stabilised zirconia is a well-studied material, voided yttria-stabilised zirconia powder particles have not been demonstrated yet, and might play an important role in future technology developments. A sol-gel synthesis accompanied by a freeze-drying process is currently being proposed as a method of obtaining sponge-like nano morphology of embedded faceted voids inside yttria-stabilised zirconia particles. The results rely on a freeze-drying stage as an effective and simple method for generating nano-voided yttria-stabilised zirconia particles without the use of template-assisted additives.