Engineered pigments based on iridescent cellulose nanocrystal films.

A simple method to produce biobased iridescent pigments from cellulose nanocrystal (CNC) films is reported. The process consists of forming nanostructured films from a CNC liquid-crystalline suspension and an appropriate dry grinding. The features of the iridescent pigments are described; they have a flake-like morphology with a thickness of 25 µm. However, because of the presence of sulfate groups, thermal degradation and high redispersion in water occur, which affect the iridescent property of these biobased pigments. To overcome such limitations, two post-treatments are proposed. The sulfate ester groups are removed from the iridescent pigments with vacuum overdrying. The mass loss of iridescent pigment in water is reduced with an increase of the ionic strength in the aqueous medium by NaCl addition. These post-treatments have proven to be efficient and engineered pigments based on CNC films can be used to add anticounterfeiting features to packaging manufactured by classical paper techniques or extrusion.

Flexibility and color monitoring of cellulose nanocrystal iridescent solid films using anionic or neutral polymers.

One property of sulfated cellulose nanocrystals (CNCs) is their ability to self-assemble from a concentrated suspension under specific drying conditions into an iridescent film. Such colored films are very brittle, which makes them difficult to handle or integrate within an industrial process. The goal of this study is (i) to produce flexible films using neutral poly(ethylene glycol) (PEG) and (ii) to modulate their coloration using an anionic polyacrylate (PAAS). The first part is dedicated to studying the physicochemical interactions of the two polymers with CNCs using techniques such as zeta potential measurements, dynamic light scattering (DLS), quartz crystal microbalance (QCM), and atomic force microscopy (AFM). Iridescent solid films were then produced and characterized using scanning electron microscopy (SEM) and UV-visible spectroscopy. The mechanical and thermal properties of films incorporating CNC were measured to evaluate improvements in flexibility. The addition of 10 wt % of PEG makes these films much more flexible (with a doubling of the elongation), with the coloration being preserved and the temperature of degradation increasing by almost 35 °C. Up to 160 µmol/gCNC PAAS can be added to tune the coloration of the CNC films by producing a more narrow, stronger coloration in the visible spectrum (higher absorption) with a well-pronounced fingerprint texture.