ABSTRACT
We report, to the best of our knowledge, the first super-octave femtosecond polycrystalline Cr:ZnS laser at the central wavelength 2.4 µm. The laser is based on a non-polarizing astigmatic X-folded resonator with normal incidence mounting of the gain element. The chromatic dispersion of the resonator is controlled with a set of dispersive mirrors within one third of an optical octave over 2.05-2.6 µm range. The resonator's optics is highly reflective in the range 1.8-2.9 µm. The components of the oscillator's output spectrum at the wavelengths 1.6 µm and 3.2 µm are detected at -60 dB with respect to the main peak. Average power of few-cycle Kerr-lens mode-locked laser is 1.4 W at the pulse repetition frequency 79 MHz. That corresponds to 22% conversion of cw radiation of Er-doped fiber laser, which we used for optical pumping of the Cr:ZnS oscillator.
ABSTRACT
We report, to the best of our knowledge, the first fully referenced Cr:ZnS optical frequency comb. The comb features few cycle output pulses with 3.25 W average power at 80 MHz repetition rate, spectrum spanning 60 THz in the middle-IR range 1.79-2.86 µm, and a small footprint (0.1 m2), The spectral components used for the measurement of the comb's carrier envelope offset frequency were obtained directly inside the polycrystalline Cr:ZnS laser medium via intrinsic nonlinear interferometry. Using this scheme we stabilized the offset frequency of the comb with the residual phase noise of 75 mrads.
ABSTRACT
It is generally accepted that chemically synthesized nanoparticles lose their ferroelectricity (spontaneous polarization) as the particles become smaller. In contrast, ball-milled ferroelectric nanoparticles have an enhanced ferroelectric response at remarkably small sizes (≤10 nm). Although prior theory suggests that surface stress influences ferroelectricity, the source of such a stress and how it physically influences ferroelectricity in zero-dimensional nanoparticles has remained a mystery. In this paper, we demonstrate that the top-down approach of wet ball-milling not only results in fragmented materials on the nanoscale, but it also is responsible for a mechanochemical synthesis of metal carboxylates forming at the nanoparticles' surface. We prove that the presence of such a compound with a particular type of binding mode chemisorbed at the nanoparticles' surface is responsible for producing surface stress. This surface stress results in a stabilization and dramatic enhancement of the spontaneous polarization, which is 5 times greater than that of the bulk material and 650 times greater than what is measured in materials fabricated using standard chemical synthesis techniques. The results of this study have further led to the development of a new process that produces ferroelectric nanoparticles (≤10 nm) with uniform shape and size using a combination of wet chemistry and mechanochemical synthesis.