Synthesis of Carbon Nanodots from Sugarcane Syrup, and Their Incorporation into a Hydrogel-Based Composite to Fabricate Innovative Fluorescent Microstructured Polymer Optical Fibers.

Carbon nanodots (CNDs) are interesting materials due to their intrinsic fluorescence, electron-transfer properties, and low toxicity. Here, we report a sustainable, cheap, and scalable methodology to obtain CNDs from sugarcane syrup using a domestic microwave oven. The CNDs were characterized by infrared spectroscopy, dynamic light scattering, atomic force microscopy, absorption, and emission spectroscopies. The CNDs have 3 nm in diameter with low polydispersity and are fluorescent. A fluorescent hydrogel-CNDs composite was obtained using gelatin polypeptide as the polymeric matrix. The new hydrogel-CNDs composite was incorporated in the cavities of a double-clad optical fiber using an innovative approach that resulted in a microstructured polymer optical fiber with intrinsic fluorescence. This work shows a promising alternative for the fabrication of fluorescent materials since the CNDs synthesis is sustainable and environmentally friendly. These CNDs might substitute the rare-earth and other heavy metals of high cost and toxicity, which are usually incorporated in double-clad fibers for applications on lasers, amplifiers, and spectroscopy.

Organoclay nanocomposites of post-industrial waste poly(butylene terephthalate) from automotive parts.

Polymeric nanocomposites are novel materials of huge interest owing to their favourable cost/performance ratio with low amount of nanofillers, improved thermal resistance, flame retardancy and mechanical properties in relation to their matrices. In this work, composites based on post-industrial waste or primary recycled poly(butylene terephthalate) and 5 wt.% of organic modified montmorillonite clays were melt compounded using a twin-screw extruder. A 2(2) factorial experimental design was used to study the compounding and processing variables: Organic modified montmorillonite with one or two hydrogenated tallow (initial basal spacing) and screw speed of the extruder. X-ray diffraction and transmission electron microscopy suggest that a partial exfoliation of the organoclay in the recycled poly(butylene terephthalate) matrix was achieved for organic modified montmorillonite with lower initial basal spacing. On the other hand, formulations containing organic modified montmorillonite with higher initial basal spacing showed only intercalated structure. The recycled poly(butylene terephthalate)-organic modified montmorillonite nanocomposites did not drip flaming material during burning tests. Storage of dynamic-mechanical, tensile and flexural moduli of the recycled poly(butylene terephthalate)-organic modified montmorillonite were improved when compared with both virgin and recycled poly(butylene terephthalate)s, mainly for nanocomposites formulated at a lower initial basal spacing organoclay. This could be related to a better diffusion of polymer into organic modified montmorillonite layers compared with the higher initial basal spacing organoclay. The improvements on the physical properties of recycled poly(butylene terephthalate) showed the feasibility to add value to primary recycled engineering thermoplastics with a very small amount of organic modified montmorillonite.