ABSTRACT
Transition metal dichalcogenides (TMDs) are regarded as a possible material platform for quantum information science and related device applications. In TMD monolayers, the dephasing time and inhomogeneity are crucial parameters for any quantum information application. In TMD heterostructures, coupling strength and interlayer exciton lifetimes are also parameters of interest. However, many demonstrations in TMDs can only be realized at specific spots on the sample, presenting a challenge to the scalability of these applications. Here, using multi-dimensional coherent imaging spectroscopy, we shed light on the underlying physics-including dephasing, inhomogeneity, and strain-for a MoSe2 monolayer and identify both promising and unfavorable areas for quantum information applications. We, furthermore, apply the same technique to a MoSe2/WSe2 heterostructure. Despite the notable presence of strain and dielectric environment changes, coherent and incoherent coupling and interlayer exciton lifetimes are mostly robust across the sample. This uniformity is despite a significantly inhomogeneous interlayer exciton photoluminescence distribution that suggests a bad sample for device applications. This robustness strengthens the case for TMDs as a next-generation material platform in quantum information science and beyond.
ABSTRACT
We report tunable excitation-induced dipole-dipole interactions between silicon-vacancy color centers in diamond at cryogenic temperatures. These interactions couple centers into collective states, and excitation-induced shifts tag the excitation level of these collective states against the background of excited single centers. By characterizing the phase and amplitude of the spectrally resolved interaction-induced signal, we observe oscillations in the interaction strength and population state of the collective states as a function of excitation pulse area. Our results demonstrate that excitation-induced dipole-dipole interactions between color centers provide a route to manipulating collective intercenter states in the context of a congested, inhomogeneous ensemble.
ABSTRACT
We characterize a high-density sample of negatively charged silicon-vacancy (SiV^{-}) centers in diamond using collinear optical multidimensional coherent spectroscopy. By comparing the results of complementary signal detection schemes, we identify a hidden population of SiV^{-} centers that is not typically observed in photoluminescence and which exhibits significant spectral inhomogeneity and extended electronic T_{2} times. The phenomenon is likely caused by strain, indicating a potential mechanism for controlling electric coherence in color-center-based quantum devices.