Effect of De-Icing Chemicals on Concrete Scaling: The Role of Storage Water.

This paper deals with the effect of the character of the water used for the water storage of concrete test specimens on the results of tests for resistance to de-icing chemicals. Two experiments were conducted to investigate the effect of the content of free CO2 in water and leaching of calcium hydroxide from concrete on the test results. In the first experiment, the resistance of mortars to water and de-icing chemicals was investigated. It was found that the character of the water storage, i.e., fresh water vs. previously used water, can significantly affect the test results. The second experiment focused on investigating the effect of the content of free CO2 in water on the test results. It was found that the content of free CO2 in the water can statistically significantly influence the test results. In conclusion, the paper shows that the character of the water used for water storage of concrete test specimens and the content of free CO2 in water are essential factors that can significantly affect the results of concrete resistance tests to de-icing chemicals. Further research is needed to understand these influences and their potential use to improve the resistance of concrete.

Electrical and Self-Sensing Properties of Alkali-Activated Slag Composite with Graphite Filler.

The electrical properties of concrete are gaining their importance for the application in building construction. In this study, graphite powder was added to alkali-activated slag mortar as an electrically conductive filler in order to enhance the mortar's conductive properties. The amount of graphite ranged from 1% to 30% of the slag mass. The effect of the graphite powder on the resistivity, capacitance, mechanical properties, and microstructure of the composite was investigated. Selected mixtures were then used for the testing of self-sensing properties under compressive loading. The results show that the addition of an amount of graphite equal to up to 10% of the slag mass improved the electrical properties of the alkali-activated slag. Higher amounts of filler did not provide any further improvement in electrical properties at lower AC frequencies but caused a strong deterioration in mechanical properties. The best self-sensing properties were achieved for the mixture with 10 wt% of graphite, but only at low compressive stresses of up to 6 MPa.