ABSTRACT
In this work, we discuss the synthesis and characterization of a 2D coordination polymer composed of a dianionic perhydroxylated boron cluster, [B12(OH)122-], coordinated to Zn(II)-the first example of a transition metal-coordinated [B12(OH)12]2- compound. This material was synthesized via cation exchange from the starting cesium salt and then subjected to rigorous characterization prior to and after thermal activation. Numerous techniques, including XRD, FTIR, SEM, TGA, and solid-state NMR revealed a 2D coordination polymer composed of sheets of Zn(II) ions intercalated between planes of boron clusters. The as-synthesized material was then evacuated of solvent via thermal treatment, and atomic-level changes from this transformation were elucidated through a combination of 1D and 2D solid-state NMR analyses of 11B and 1H nuclei, suggesting the full removal of coordinated solvent molecules. Evidence also suggested that [B12(OH)122-] can adjust its coordination to Zn(II) in the solid-state through hemilability of its numerous -OH ligands.
ABSTRACT
The synthesis, characterization, and electrocatalytic properties of mesoporous carbon materials doped with nitrogen atoms and iron are reported and compared for the catalyzed reduction of oxygen gas at fuel cell cathodes. Mixtures of common and inexpensive organic precursors, melamine, and formaldehyde were pyrolyzed in the presence of transition-metal salts (e.g., nitrates) within a mesoporous silica template to yield mesoporous carbon materials with greater extents of graphitization than those of others prepared from small-molecule precursors. In particular, Fe,N-doped carbon materials possessed high surface areas (â¼800 m2/g) and high electrical conductivities (â¼19 S/cm), which make them attractive for electrocatalyst applications. The surface compositions of the mesoporous Fe,N-doped carbon materials were postsynthetically modified by acid washing and followed by high-temperature thermal treatments, which were shown by X-ray photoelectron spectroscopy to favor the formation of graphitic and pyridinic nitrogen moieties. Such surface-modified materials exhibited high electrocatalytic oxygen reduction activities under alkaline conditions, as established by their high onset and half-wave potentials (1.04 and 0.87 V, respectively vs reversible hydrogen electrode) and low Tafel slope (53 mV/decade). These values are superior to many similar transition-metal- and N-doped carbon materials and compare favorably with commercially available precious-metal catalysts, e.g., 20 wt % Pt supported on activated carbon. The analyses indicate that inexpensive mesoporous Fe,N-doped carbon materials are promising alternatives to precious metal-containing catalysts for electrochemical reduction of oxygen in polymer electrolyte fuel cells.