ABSTRACT
In the current study, nanocrystalline CoY0.5xLa0.5xFe2-xO4 (where x = 0.00, 0.02, 0.04, 0.06, 0.08, and 0.10) ferrites have been synthesized via a sol-gel auto combustion process. The synthesized powders were pressed into pellet forms and sintered at 900 °C for 4 h in the air. X-ray diffractometry (XRD) confirmed the single-phase cubic spinel structure of the synthesized samples having the mean crystallite domain sizes ranging from 122 and 54 nm. FTIR spectroscopic analyses revealed two strong bands within the range of 600 to 350 cm-1, further confirming the cubic inverse spinel structure of the prepared materials. The surface morphologies and composition were investigated by Field Emission Scanning Electron Microscopy (FE-SEM) and Energy Dispersive X-ray (EDX) Spectroscopy. The magnetic hysteresis curves recorded at room temperature exhibit ferrimagnetic behavior. The highest coercivity (Hcâ¼1276 Oe) was found at a high doping (x = 0.10) concentration of Y3+ and La3+ in cobalt ferrite. Dielectric constant increase with increased doping concentration whereas real-impedance and dielectric loss decrease with increased in doping concentration and applied frequency. The band gap energy increased from 1.48 to 1.53 eV with increasing Y3+ and La3+concentrations in the UV-Vis region. The elevated levels of magnetic and dielectric substances in the ferrite nanoparticles suggest that the material could be used for magnetic recording media and high-frequency devices.
ABSTRACT
Herein, paper mill waste sludge (PMS) from two different sources has been investigated to extract calcium hydroxide, Ca(OH)2 by a facile and inexpensive extraction process. PMS samples, collected from local paper mill plants of Bangladesh, were the main precursors wherein HCl and NaOH were used for chemical treatment. The as-synthesized products were analysed by a variety of characterization tools including X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, Raman spectroscopy, scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) elemental analyses. Our studies confirm that the extracted product contains Ca(OH)2 as a major content, albeit it also includes CaCO3 phase owing to the inescapable carbonation process from the surrounding environment. The particle size of the synthesized products is in the range of 450-500 nm estimated from SEM micrographs. The crystallite domain size of the same estimated from XRD analyses and was found to be approximately 47 and 31 nm respectively for product-A and product-B considering major (101) Bragg peak of Ca(OH)2. The yield percentage of the isolated products is about 65% for samples collected from both sources.