ABSTRACT
Magnetic metallic nanoparticles (MNPs) of Ni, Ni82Fe18, Ni50Fe50, Ni64Fe36, and Fe were prepared by the technique of the electrical explosion of metal wire. The average size of the MNPs of all types was in the interval of 50 to 100 nm. Magnetic polymeric composites based on polyvinyl butyral with embedded metal MNPs were synthesized and their structural, adhesive, and magnetic properties were comparatively analyzed. The interaction of polyvinyl butyral (supplied as commercial GE cryogenic varnish) with metal MNPs was studied by microcalorimetry. The enthalpy of adhesion was also evaluated. The positive values of the enthalpy of interaction with GE increase in the series Ni82Fe18, Ni64Fe36, Ni50Fe50, and Fe. Interaction of Ni MNPs with GE polymer showed the negative change in the enthalpy. No interfacial adhesion of GE polymer to the surface of Fe and permalloy MNPs in composites was observed. The enthalpy of interaction with GE polymer was close to zero for Ni95Fe5 composite. Structural characterization of the GE/Ni composites with the MNPs with the lowest saturation magnetization confirmed that they tended to be aggregated even for the materials with lowest MNPs concentrations due to magnetic interaction between permalloy MNPs. In the case of GE composites with Ni MNPs, a favorable adhesion of GE polymer to the surface of MNPs was observed.
ABSTRACT
Present day biomedical applications, including magnetic biosensing, demand better understanding of the interactions between living systems and magnetic nanoparticles (MNPs). In this work spherical MNPs of maghemite were obtained by a highly productive laser target evaporation technique. XRD analysis confirmed the inverse spinel structure of the MNPs (space group Fd-3m). The ensemble obeyed a lognormal size distribution with the median value 26.8 nm and dispersion 0.362. Stabilized water-based suspensions were fabricated using electrostatic or steric stabilization by the natural polymer chitosan. The encapsulation of the MNPs by chitosan makes them resistant to the unfavorable factors for colloidal stability typically present in physiological conditions such as pH and high ionic force. Controlled amounts of suspensions were used for in vitro experiments with human blood mononuclear leukocytes (HBMLs) in order to study their morphofunctional response. For sake of comparison the results obtained in the present study were analyzed together with our previous results of the study of similar suspensions with human mesenchymal stem cells. Suspensions with and without chitosan enhanced the secretion of cytokines by a 24-h culture of HBMLs compared to a control without MNPs. At a dose of 2.3, the MTD of chitosan promotes the stimulating effect of MNPs on cells. In the dose range of MNPs 10-1000 MTD, chitosan "inhibits" cellular secretory activity compared to MNPs without chitosan. Both suspensions did not caused cell death by necrosis, hence, the secretion of cytokines is due to the enhancement of the functional activity of HBMLs. Increased accumulation of MNP with chitosan in the cell fraction at 100 MTD for 24 h exposure, may be due to fixation of chitosan on the outer membrane of HBMLs. The discussed results can be used for an addressed design of cell delivery/removal incorporating multiple activities because of cell capability to avoid phagocytosis by immune cells. They are also promising for the field of biosensor development for the detection of magnetic labels.
Subject(s)
Magnetite Nanoparticles , Chitosan , Ferric Compounds , Humans , Materials Testing , Static Electricity , Suspensions , WaterABSTRACT
A new kind of ferrogel with entrapped metallic iron nanoparticles causing unusual magnetodeformation is presented. Crosslinked polyacrylamide (PAAm) based ferrogels embedded with iron nanoparticles (MNPs) were synthesized by free radical polymerization in aqueous medium. Spherical iron MNPs with average diameter 66 nm were synthesized by the electrical explosion of wire and modified by interfacial adsorption of linear polyacrylamide (LPAAm). Extended Derjaguin-Landau-Verwey-Overbeek (xDLVO) calculations based on the superposing of van der Waals, electrostatic, steric, and magnetic contributions showed that polymeric encapsulation of nanoparticles by LPAAm is one of the most suitable pathways for preparing stable aqueous dispersions of iron nanoparticles. Microcalorimetry confirmed the presence of strong interfacial adhesion forces between LPAAm chains and the surface of iron nanoparticles. By keeping the same crosslinking density of a polymer network (i.e. 100 : 1, monomer to crosslinker ratio) and varying the initial monomer concentration, an influence of the extent of polymer network reticulation on the mechanical properties and subsequently, magneto-elastic properties was demonstrated. It was found that the upper limit of the shear modulus for the synthesis of a new kind of polyacrylamide based ferrogel to exhibit any usable magnetodeformation under the application of a uniform external magnetic field of 420 mT is ca. 1 kPa. Magnetodeformation of cylindrical ferrogel samples was observed in the form of an overall volume contraction accompanied by a homogeneous decrease in all dimensions. The deformation was found to be maximum (around 10%) for the aspect ratio of 1/1 and it was lower and similar for the samples with 1/2 and 2/1 aspect ratios. Such a type of magnetic response is significantly different from the behavior observed in the existing reports on ferroelastomers.