ABSTRACT
Laser synthesis was used for one-step synthesis of titania/graphene composites (G-TiO2 (C)) from a suspension of 0.04 wt% commercial reduced graphene oxide (rGO) dispersed in liquid titanium tetraisopropoxide (TTIP). Reference titania sample (TiO2(C)) was prepared by the same method without graphene addition. Both samples and commercial titania P25 were characterized by various methods and tested under UV/vis irradiation for oxidative decomposition of acetic acid and dehydrogenation of methanol (with and without Pt co-catalyst addition), and under vis irradiation for phenol degradation and inactivation of Escherichia coli. It was found that both samples (TiO2(C) and G-TiO2(C)) contained carbon resulting from TTIP and C2H4 (used as a synthesis sensitizer), which activated titania towards vis activity. The photocatalytic activity under UV/vis irradiation was like that by P25. The highest activity of TiO2(C) sample for acetic acid oxidation was probably caused by its surface enrichment with hydroxyl groups. G-TiO2(C) was the most active for methanol dehydrogenation in the absence of platinum (ca. five times higher activity than that by TiO2(C) and P25), suggesting that graphene works as a co-catalyst for hydrogen evolution. High activity under both UV and vis irradiation for decomposition of organic compounds, hydrogen evolution and inactivation of bacteria suggests that laser synthesis allows preparation of cheap (carbon-modified) and efficient photocatalysts for broad environmental applications.
ABSTRACT
This work presents an original synthesis of TiO2/graphene nanocomposites using laser pyrolysis for the demonstration of efficient and improved perovskite solar cells. This is a one-step and continuous process known for nanoparticle production, and it enables here the elaboration of TiO2 nanoparticles with controlled properties (stoichiometry, morphology, and crystallinity) directly grown on graphene materials. Using this process, a high quality of the TiO2/graphene interface is achieved, leading to an intimate electronic contact between the two materials. This effect is exploited for the photovoltaic application, where TiO2/graphene is used as an electron-extracting layer in n-i-p mesoscopic perovskite solar cells based on the reference CH3NH3PbI3-x Cl x halide perovskite active layer. A significant and reproducible improvement of power conversion efficiencies under standard illumination is demonstrated, reaching 15.3% in average compared to 13.8% with a pure TiO2 electrode, mainly due to a drastic improvement in fill factor. This beneficial effect of graphene incorporation is revealed through pronounced photoluminescence quenching in the presence of graphene, which indicates better electron injection from the perovskite active layer. Considering that a reduction of device hysteresis is also observed by graphene addition, the laser pyrolysis technique, which is compatible with large-scale industrial developments, is therefore a powerful tool for the production of efficient optoelectronic devices based on a broad range of carbon nano-objects.